Aspects Of The Residual-Stress Field At A Notch And Its Effect On Fatigue

Dq Zhang,Kw Xu,Jw He

DOI: https://doi.org/10.1016/0921-5093(91)90443-Q

1991-01-01

Abstract:X-ray stress measurements for a 1 mm radius notch were carried out and a residual stress distribution, induced by shot peening in the notched part, was detected. It is shown that the residual stress exhibits a concentration effect at the notch, but the concentration factor is different from that of the loading stress. The residual stress concentration is related to the shape of the specimen and the strength of the material. The fatigue limits of medium carbon steel specimens were tested with rotating bending. The compressive residual stress at the notch part of a specimen tempered at high temperature relaxes rapidly under cyclic loading; the increase in the fatigue limit after shot peening shows more or less the same behaviour as that of a smooth specimen treated in the same way. In contrast, a great improvement in the notch fatigue limit is observed for a specimen tempered at low temperature with a high yield strength. A biaxial shear stress model is used to explain the residual stress relaxation; this model agrees with the experimental data and is better than the Von Mises criterion.