Glass-ceramics synthesis using the collaborative smelting slag of spent automotive catalyst and copper-bearing electroplating sludge
Ruili Zheng,Jianfang Lyu,Weifeng Song,Mudan Liu,Huashan Li,Yong Liu,Xianjin Lyu,Zhiyuan Ma
DOI: https://doi.org/10.1016/j.seppur.2022.122985
IF: 8.6
2022-12-26
Separation and Purification Technology
Abstract:This paper studied the glass-ceramics preparation from the collaborative smelting slag of spent automotive catalyst (SAC) and copper-bearing electroplating sludge (CBES) by the one-step sintering method without additional nucleating agents. The crystallization mechanism, including nucleation and crystal growth steps, was investigated by DSC, XRD and FETEM-EDS. The crystallization process during heat treatment could be summarized as follows: Fe 3+ ions will congregate firstly in a small range on the surface and inside of the originally homogeneous amorphous matrix, and then gradually crystallize and transform into stable hematite (Fe 2 O 3 ) crystal nuclei. Augite and gehlenite as the main two crystalline phases grow around hematite (Fe 2 O 3 ) epitaxially. Additionally, the surface crystallization dominates the overall process based on the crystallization kinetics calculation. The optimum sintering temperatures of glass-ceramics preparation were researched according to the physicochemical properties analysis. When the sintering temperatures are 850°C−875°C, the density, water absorption, Vickers hardness, flexible strength, acid and alkali resistance of glass-ceramics products are 2.8–2.9 g/cm 3 , 0.08%–0.09%, 6.5–6.7 GPa, 98–115 MPa, 96.6%–96.9% and 98.5%–99.6%, respectively. Toxicity characteristic leaching procedure (TCLP) test shows that the material can be taken as non-hazardous. This work realizes resource utilization and detoxification of the co-smelting slag of SAC and CBES.
engineering, chemical