Preparation of glass ceramic by low-temperature melting of municipal solid waste incineration fly ash and municipal sludge

Jinxin Xing,Qingyu Tang,Min Gan,Zhiyun Ji,Xiaohui Fan,Zengqing Sun,Xuling Chen,Qiang Jing
DOI: https://doi.org/10.1016/j.matlet.2024.135962
IF: 3
2024-03-01
Materials Letters
Abstract:Utilization of municipal solid waste, such as incineration fly ash (MFA) and municipal sludge (MS), is currently the focus area of research. In this paper, glass ceramics were prepared from these two types of municipal solid waste. The melting temperature could be reduced through the component regulation, thus lowering the production cost of glass ceramics. The results indicated that glass ceramics were successfully prepared at the temperatures below 1300 °C and the MFA/MS ratio of 1:1 – 3:7. The morphostructural analysis of glass ceramics revealed the formation of abundant crystals and fine grains. The volume density of ceramics was 2.82–2.92 g/cm3. The Vickers hardness of glass ceramics was greater than 6.68 GPa and the best fracture toughness was 5.85 MPa•m1/2; meanwhile, the acid and alkali corrosion resistance was above 96 %. These results suggest the feasibility of preparation of glass ceramics with good performance from MFA and MS at relatively low temperatures.
materials science, multidisciplinary,physics, applied
What problem does this paper attempt to address?