Growth and Properties of TSAG and TSLAG Magneto-Optical Crystals with Large Size
Renqin Dou,Haotian Zhang,Qingli Zhang,Naifeng Zhuang,Wenpeng Liu,Yi He,Yingying Chen,Maojie Cheng,Jianqiao Luo,Dunlu Sun
DOI: https://doi.org/10.1016/j.optmat.2019.109272
IF: 3.754
2019-01-01
Optical Materials
Abstract:Large size high transparent TSAG and TSLAG single crystals of empty set 65 mm x 70 mm have been grown successfully by the Cz method. The refractive indices at 473, 532, 632.8 and 1064 nm are 1.9214 - 1.8817 for TSAG and 1.9242 - 1.8841 for TSLAG. Their Sellmeier equations are fitted. The average thermal expansion coefficients of TSAG and TSLAG at 300 - 373 K, 300 - 473 K, 300 - 573 K, 300 - 673 K, and 300 - 773 K are measured. The values of thermal expansion coefficients of TSAG and TLSAG crystals coincide within the measurement error (differ by 0.3-0.4%). The thermal diffusivity values of TSAG and TSLAG are 1.454 and 1.418 mm(2) s(-1) at 300 K, respectively. Calculated with the specific heat results, the values of thermal conductivity of TSAG and TSLAG are 4.45 and 4.20 W (m K)(-1) at 300 K. Moreover, the Verdet constants of TSAG are 218, 152, and 65 rad/m/T at 532, 633, and 1064 can, while those of TSLAG are 246, 146, and 56 rad/m/T, respectively. In further, the relationships between Verdet constant and wavelength of TSAG and TSLAG are obtained.