Abstract:A catalytic ozonation advanced oxidation process (AOP) with a copper(II)-doped carbon dot as catalyst, Cu-CD (using L-cysteine and polyethylene glycol (PEG) as precursors and passivation agents), was developed for textile wastewater treatment (T = 25 °C and pH = 7). Four dyes were analyzed—Methyl Orange (MO), Orange II sodium salt (O-II), Reactive Black 5 (RB-5) and Remazol Brilliant Blue R (RBB-R), as well as a real effluent from the dying and printing industry. The Cu-CD, with marked catalytic ozonation properties, was successfully synthesized by one-pot hydrothermal procedure with a size of 4.0 nm, a charge of −3.7 mV and a fluorescent quantum yield of 31%. The discoloration of the aqueous dye solutions followed an apparent first-order kinetics with the following rate constants (kap in min−1): MO, 0.210; O-II, 0.133; RB-5, 0.177; RBB-R, 0.086. In the presence of Cu-CD, the following apparent first-order rate constants were obtained (kapc in min−1) with the corresponding increase in the rate constant without catalyst (%Inc): MO, 1.184 (464%); O-II, 1.002 (653%); RB-5, 0.709 (301%); RBB-R, 0.230 (167%). The presence of sodium chloride (at a concentration of 50 g/L) resulted in a marked increase of the discoloration rate of the dye solution due to generation of other radicals, such as chlorine and chlorine oxide, resulting from the reaction of ozone and chloride. Taking into consideration that the real textile effluent under research has a high carbonate concentration (>356 mg/L), which inhibits ozone decomposition, the discoloration first-order rate constants without and with Cu-CD (kap = 0.0097 min−1 and kapc = 0.012 min−1 (%Inc = 24%), respectively) were relatively small. Apparently, the Cu-CD, the surface of which is covered by a soft and highly hydrated caramelized PEG coating, accelerates the ozone decomposition and dye adsorption, increasing its degradation.

Copper/activated Carbon As Catalyst for Organic Wastewater Treatment

Homogeneous Catalytic Wet‐Air Oxidation for the Treatment of Textile Wastewater

Enhanced Conversion from H2O2 to 1O2 on Cu–N Centers: Investigation of Mechanisms and Application in Alkaline Wastewater Treatment

Advanced Progress in Treatment and Resource Utilization of Copper Containing Wastewater

Studies on Copper Catalysts for Wet Air Oxidation of High Concentration Coking-Plant Wastewater

Catalytic Oxidation of Dyeing Wastewater by Copper Oxide Activating Persulfate: Performance, Mechanism and Application

Fabrication of MnOx heterogeneous catalysts from wet sludge for degradation of azo dyes by activated peroxymonosulfate

Copper(II)-Doped Carbon Dots as Catalyst for Ozone Degradation of Textile Dyes

Dithionite accelerated copper slag heterogeneous-homogeneous coupled Fenton degradation of organic pollutants

A New Catalyst CHCP-Fe2O3 for Enhanced Removal of Tetracycline Through the Fenton-like Process: Economical Synthesis, Catalytic Performance, and Practicability

Catalytic Ozonation with Carbon-Coated Copper-based Core-shell Catalysts (C/Cu-Al2O3) for the Treatment of High-Salt Petrochemical Wastewater

Superior Degradation Performance of Nanoporous Copper Catalysts on Methyl Orange

TREATMENT OF MOLASSES ALCOHOL WASTEWATER BY INTERNAL ELECTROLYSIS

Photocatalytic Oxidation of Printing and Dyeing Wastewater by Foam Ceramics Loaded with Cu and N–TiO2

Preparation of Heterogeneous Fenton Catalysts Cu-Doped MnO2 for Enhanced Degradation of Dyes in Wastewater

Novel catalysts with multivalence copper for organic pollutants removal from wastewater with excellent selectivity and stability in Fenton-like process under neutral pH conditions

Exploration of Copper-Cysteamine Nanoparticles As an Efficient Heterogeneous Fenton-like Catalyst for Wastewater Treatment

Catalytic wet peroxide oxidation of aniline in wastewater using copper modified SBA-15 as catalyst

3D Printing and Chemical Dealloying of a Hierarchically Micro- and Nanoporous Catalyst for Wastewater Purification

Preparation and Structural Characterization of Copper Catalysts for Water Treatment

Sustainable upcycling of copper from waste printed circuit boards with the assistance of tannic acid and Fe3+ to a magnetic heterogeneous catalyst