Abstract:Activated carbons (ACs) have been the most widespread carbon materials used in supercapacitors (SCs) due to their easy processing methods, good electrical conductivity, and abundant porosity. For the manufacture of electrodes, the obtained activated carbon based on sawdust (karagash and pine) was mixed with conductive carbon and polyvinylidene fluoride as a binder, in ratios of 75% activated carbon, 10% conductive carbon black, and 15% polyvinylidene fluoride (PVDF) in an N-methyl pyrrolidinone solution, to form a slurry and applied to a titanium foil. The total mass of each electrode was limited to vary from 2.0 to 4.0 mg. After that, the electrodes fitted with the separator and electrolyte solution were symmetrically assembled into sandwich-type cell construction. The carbon's electrochemical properties were evaluated using cyclic voltammetry (CV) and galvanostatic charge-discharge (CGD) studies in a two-electrode cell in 6M KOH. The CV and CGD measurements were realized at different scan rates (5-160 mV s-1) and current densities (0.1-2.0 A g-1) in the potential window of 1 V. ACs from KOH activation showed a high specific capacitance of 202 F g-1 for karagash sawdust and 161 F g-1 for pine sawdust at low mass loading of 1.15 mg cm-2 and scan rate of 5 mV s-1 in cyclic voltammetry test and 193 and 159 F g-1 at a gravimetric current density of 0.1 A g-1 in the galvanostatic charge-discharge test. The specific discharge capacitance is 177 and 131 F g-1 at a current density of 2 A g-1. Even at a relatively high scan rate of 160 mV s-1, a decent specific capacitance of 147 F g-1 and 114 F g-1 was obtained, leading to high energy densities of 26.0 and 22.1 W h kg-1 based on averaged electrode mass. Surface properties and the porous structure of the ACs were studied by scanning electron microscopy, energy-dispersive X-ray analysis, Raman spectroscopy, and the Brunauer-Emmett-Teller method.

Electrochemical Behavior of Activated Carbon for the Asymmetric Supercapacitor

Facile Activation of Commercial Carbon Felt As a Low-Cost Free-Standing Electrode for Flexible Supercapacitors

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Boosting Supercapacitive Performance of Flexible Carbon Via Surface Engineering.

Electrochemical Profile of an Asymmetric Supercapacitor Using Carbon-Coated LiTi2(PO4)3 and Active Carbon Electrodes

Impedance Spectroscopy of Symmetric and Asymmetric Supercapacitors

Asymmetric Supercapacitors Based On Graphene/Mno2 And Activated Carbon Nanofiber Electrodes With High Power And Energy Density

Preparation and Electrochemical Performance of Hollow Activated Carbon Fiber Self-Supported Electrode for Supercapacitor

An Aqueous Asymmetric Supercapacitor Based on Activated Carbon and Tungsten Trioxide Nanowire Electrodes

Activated‐carbon‐based supercapacitors with high gravimetric‐ and volumetric capacitance at commercial‐level mass loading

Activator concentration regulating the porous structure of activated carbon for supercapacitor application

The performance of LiMn2O4/activated carbon supercapacitor

Electrochemical Performance of Chemically Activated Carbons from Sawdust as Supercapacitor Electrodes

Nickel Sulfide/activated Carbon Nanotubes Nanocomposites As Advanced Electrode of High-Performance Aqueous Asymmetric Supercapacitors

MXene-MnO2-CoNi layered double hydroxides//activated carbon flexible asymmetric supercapacitor

Enhancing the Capacity of Activated Carbon Electrodes by a Redox Mediator Pair for the Fabrication of Flexible Asymmetric Solid-State Supercapacitors

PREPARATION AND ELECTROCHEMISTRY PROPERTIES OF ACTIVATED CARBON ELECTRODE FOR SUPERCAPACITOR

Study on Influencing Factors of Energy-storage of the Activated Carbon Electrodes for Supercapacitors

An Asymmetric Supercapacitor Based on a NiO/Co3O4@NiCo Cathode and an Activated Carbon Anode

Electrochemical Performance of Graphene-Coated Activated Mesocarbon Microbeads As a Supercapacitor Electrode

A high-performance supercapacitor based on activated carbon fibers with an optimized pore structure and oxygen-containing functional groups