Abstract:We report the structural and magnetic properties of zinc-nickel ferrites (ZNF), Zn1−x Ni x Fe2O4, nanoparticles synthesized by the hydrothermal method with 0.0 ≤ x ≤ 1.0. The X-ray powder diffraction of Zn1−x Ni x Fe2O4 shows the formation of a single spinel phase of ZnFe2O4 or NiFe2O4. The lattice parameter and unit cell volume decreased slightly as the x ratio increased, whereas the average crystallite size ranged from 9.55 to 22.7 nm. The nanoparticles’ morphology consists of small cubic and spherical particles with an average size increasing up to x = 0.6 and dropping at further increases of x. The assigned peaks obtained by the Fourier-transform infrared spectroscopy at 556–592 cm−1 verified the formation of metal (Zn, Ni, and Fe) oxides. The surface area, pore radius, and total pore volume were estimated using the Brunauer-Emmett-Teller (BET) and Barrett-Joyner-Halenda (BJH) theories and found to be dependent on the composition of the synthesized nanoferrites. Interestingly, we observed the largest surface area, S BET, of 264 ± 28 m2 g−1 at x = 0.6, which is three times higher than the other samples. The Zn1−x Ni x Fe2O4 nanoferrites exhibited ferromagnetic behavior at room temperature with a saturation magnetization between 30.3 ± 0.01 and 126 ± 0.07 emu g−1. We found a possible link between maximum retentivity, corrective filed, and squareness with the surface area, especially at x = 0.6. The magnetic behavior at x = 0.4 could be attributed to the sample’s larger crystallite/particle sizes as compared to the other samples. Our results of the synthesized Zn1−x Ni x Fe2O4 nanoparticles demonstrate the wide applicability of the ZNF nanostructures in magnetic storage as well as other applications that demand ferrite materials with a larger surface area.

Synthesis of nanosized nickel ferrites by shock waves and their magnetic properties

Mechanochemical synthesis of nanocrystalline Ni-Zn ferrite

Shock wave-induced switchable magnetic phase transition behaviour of ZnFe2O4 ferrite nanoparticles

Controlled Synthesis of Magnetic Spinel-Type Nickel Ferrite Nanoparticles by the Interface Reaction and Hydrothermal Crystallization

A self-propagating high-temperature synthesis method for Ni-ferrite powder synthesis

Rapid Synthesis Of Nickel Ferrite Nanoparticles By The Molten Salt Method

Effect of reaction condition on microstructure and properties of (NiCuZn)Fe2O4 nanoparticles synthesized via co-precipitation with ultrasonic irradiation

Synthesis of Nickel-Based Ferrite Nanofibers and Their Static Magnetic and Microwave Absorption Properties

Chemical Synthesis and Magnetic Properties of Monodisperse Nickel Ferrite Nanoparticles for Biomedical Applications

Nanoarchitectonics of zinc nickel ferrites by the hydrothermal method for improved structural and magnetic properties

Synthesis of Nanoparticles of Li Ferrite by Solid State Method

Preparation and Properties of Nanosize MnZn Ferrite from Δ-Feooh

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Self-propagating High Temperature Synthesis of Ni0.35Zn0.65Fe2O4 Ferrite Powders

Impact of Shock Compression on the Photovoltaic Performance of NiCo2O4 Nanoparticles

Microwave-polyol Controlled Synthesis and Magnetic Properties of Monodisperse CoxNi1−xFe2O4/MWCNT Nanocomposites

Metallic Iron Nanoparticles: Flame Synthesis, Characterization and Magnetic Properties

Single-Step Synthesis of Nanocrystalline Fe-Ni/Fe-Co-Ni Magnetic Alloy Coating via Directional Plasma Spray

Self-propagating High Temperature Synthesis of Ni<SUB>0.35</SUB>Zn<SUB>0.65</SUB>Fe<SUB>2</SUB>O<SUB>4</SUB> using Various Ni-containing Species

Synthesis of Nickel-Zinc Ferrite Nanoparticles by the Sol-Gel Auto-Combustion Method: Study of Crystal Structural, Cation Distribution, and Magnetic Properties

Phase formations and magnetic properties of single crystal nickel ferrite (NiFe2O4) with different morphologies