Abstract:A novel method for preparation of magnetic composite microspheres was developed by emulsifier-free emulsion polymerization controlled by 1, 1-diphenylethylene (DPE) as free radical polymerization control agent. This paper reported the synthesis of clean composite microspheres with high magnetite content and carboxylic surface by this method. The synthetic strategy is a two-step polymerization. First, some amount of acrylic acid (AA), methyl methacrylate (MMA) and DPE reacted for a few minutes in the presence of persulfate potassium (KPS) as initiator. Subsequently, Fe3O4/SiO2 magnetic fluid prepared by surface modification of Fe3O4 nanoparticles with ethyl orthosilicate was added, and the mixture was further polymerized for another time period Then the system was cooled down to room temperature. The reaction stopped and a precursor polymer which possessed amphiphilic nature and DPE-capped chains was obtained. One end of the precursor polymer chain was linked to the surface of magnetic fluid through chemical adsorption. This not only improved the hydrophobicity of magnetic fluid surface, which stabilized inorganic particles in oil monomers, but also immobilized the potential active species on the surface of nanoparticles. Secondly, the system was heated to a desired temperature and styrene (St) was added to the mixture. The DPE-containing precursor polymer was activated and initiated the monomer polymerization on the surface of magnetic nanoparticles. After a desired reaction time, some amount of acrylic acid was introduced to the system and polymerized for additional hours. At last Fe3O4/SiO2/P (AA-MMA-St) magnetic composite microspheres were obtained. The chemical structure of magnetic fluid and composite microspheres were characterized by Fourier transform infrared spectrometer (FTIR), X-ray photoelectron spectra (XPS). The carboxyl content on the surface of composite microspheres was determined by conductometric titration. The thermoanalysis of composite microspheres was conducted by differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA). The morphologies of magnetic fluid and composite microspheres were observed under a transmission electron microscope (TEM). Particle size determination of composite microsphere was conducted on a laser particle analyzer. The magnetic properties of all magnetic particles obtained were evaluated by using a vibrating-sample magnetometer (VSM). The results of FTIR and XPS indicated the hydrolysate of ethyl orthosilicate formed SiO2 layers on the surface of Fe3O4 nanoparticles. The SiO2 layer made the saturation magnetization of Fe3O4/SiO2 fall by 3.7% in contrast with Fe3O4, but it prevented Fe3O4 from reacting with-COOH group, and improved the magnetic property of Fe3O4/SiO2/P (AA-MMA-St) by 28% compared with Fe3O4/SiO2/P (AA-MMA-St) obtained at the same experimental conditions. The TEM observation suggested the composite microspheres possessed core-shell structure. The particle size measurements disclosed the average diameter of composite microspheres was 422 nm and the particle size distribution was narrow, which indicated all the monomers polymerization on the surface of magnetic nanoparticles were controlled effectively by DPE.The TGA analysis revealed the content of inorganic particle(Fe3O4/SiO2) was about 40% in composite microspheres. The magnetic property evaluation indicated the saturation magnetization of Fe3O4/SiO2/P (AA-MMA-St) was 34.850 emu/g. The conductometric titration result demonstrated the content of carboxyl group on composite microspheres surface was 0.176 mmol/g. DSC analysis showed the glass transition temperature of Fe3O4/SiO2/P (AA-MMA-St) increased by 8.9 degrees C compared with the copolymer of P(AA-MMA-St), which confirmed there was interaction between the core of magnetic nanoparticles and the shell of copolymer.

Fe<sub>3</sub>O<sub>4</sub>/poly(<i>N</i>-Isopropylacrylamide)/Chitosan Composite Microspheres with Multiresponsive Properties

Preparation and Characterization of Multiresponsive Polymer Composite Microspheres with Core–shell Structure

Preparation and Characterization of Composite Microspheres with Magnetic and Temperature Dual Stimuli-Responsive Properties

Synthesis and characterization of Fe3O4/PPy/P(MAA-co-AAm) trilayered composite microspheres with electric, magnetic and pH response characteristics

One-pot Synthesis of Poly(n-Isopropylacrylamide)/chitosan Composite Microspheres Via Microemulsion.

Temperature/pH Dual-Responsive Poly (N-Isopropylacrylamide)/chitosancoated Luminescent Composite Nanospheres: Fabrication and Controllable Luminescence

Multi-Functional Thermosensitive Composite Microspheres with High Magnetic Susceptibility Based on Magnetite Colloidal Nanoparticle Clusters

Preparation and Characterization of Thermosensitive Organic–inorganic Hybrid Microgels with Functional Fe3O4 Nanoparticles As Crosslinker

Fabrication Of Flocculation-Resistant Ph/Ionic Strength/Temperature Multiresponsive Hollow Microspheres And Their Controlled Release

Preparation of Thermoresponsive Fe3o4/P(Acrylic Acid-Methyl Methacrylate-N-Isopropylacrylamide) Magnetic Composite Microspheres with Controlled Shell Thickness and Its Releasing Property for Phenolphthalein

Preparation and Characterization of P(NIPAM-co-AA)/Fe_3O_4 Composite Microspheres

Preparation of Magnetic Temperature-responsive Composite Microspheres and Their Drug-release Behaviors Under AC Magnetic Field

Preparation of pH-responsive Fe3O4/Poly (acrylic acid-stat-methyl methacrylate-block-(2-dimethylamino) ethyl methacrylate) magnetic composite microspheres and its application in controlled release of drug

Synthesis and adsorption properties of composite microsphere with dual-magnetic responses

Flower‐Like SiO2‐Coated Polymer/Fe3O4 Composite Microspheres of Super‐Paramagnetic Properties: Preparation Via A Polymeric Microgel Template Method

Synthesis and Characterization of Fe_3O_4/SiO_2/CMCH/CdTe Fluorescent/Magnetic Microspheres

PREPARATION OF Fe3O4/SiO2/P(AA-MMA-St) MAGNETICCOMPOSITE MICROSPHERES BY CONTROLLED RADICAL POLYMERIZATION

Thermoresponsive Hollow Magnetic Microspheres With Hyperthermia And Controlled Release Properties

Hydrophilic Dual‐responsive Magnetite/pmaa Core/shell Microspheres with High Magnetic Susceptibility and Ph Sensitivity Via Distillation‐precipitation Polymerization

Magnetic thermosensitive core/shell microspheres: synthesis, characterization and performance in hyperthermia and drug delivery