Abstract:Multi-principal component alloy has been proved to form disordered solid solution in most cases. However, multi-principal component alloy with single phase solid solution has a few disadvantages in mechanical properties, such as low strength or poor plasticity. Aiming at CoCrNi-based multi-principal component alloy with low strength, this paper proposed a method to enhance the multi-principal component alloy through composition design. CoCrNiVAlx multi-principal component alloy was melted by non-consumable vacuum arc melting, and the content of σ phase in the multi-principal component alloy was changed by adjusting the content of Al element. With the addition of Al element, the fcc disordered phase in the multi-principal component alloy gradually went to the ordered L12 phase with the same structure. When the amount of Al was 1.5 wt%, the compressive strength reached 2347 MPa and the hardness reached 760.8HV, which were 30% and 20% higher than the compressive strength (1828 MPa) and hardness (619.3HV) of CoCrNiV multi-principal component alloy, respectively. With the further increase of Al element to 2.0 wt%, the σ phase in the multi-principal component alloy increased further, resulting in the simultaneous decrease of strength and plasticity. The strengthening mechanism of multi-principal component alloy was analyzed, and the strengthening action of L12 phase was confirmed. The results showed that the strengthening of multi-principal component alloy was mainly provided by L12 phase strengthening (1229.55 MPa, 52.39%) and grain boundary strengthening (376 MPa, 16.02%). This paper provided a probable strategy to increase the strength of the multi-principal component alloy, which opened up a new idea for the composition design of multi-principal component alloy.

Microstructure and Properties of Multi-principal Elements Alloy AlCrMnFeNiCu_x

Study on Microstructure and Mechanical Properties of CrCuFeNiV Multi Principal Element Alloy

Microstructure and Mechanical Properties of CoCrNiVAlx Multi-Principal Component Alloy

Influence of Cr on Microstructure and Electrochemical Properties of FeNiMnCuCrx High-entropy Alloy

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Study on Microstructure and Mechanical Properties of AlxCrFeNiCuVTi High-entropy Alloy

Insight into the Microstructure and Micromechanical Behavior and Mechanism of the Constitutional Phase of FeNiCrAl0.63 Multi-Principal Element Alloy

Unveiling the Precipitation Behavior and Mechanical Properties in G-phase Strengthened CrFe2Ni2Ti0.2Six Multi-Principal Element Alloys

Effect of Cr on solidification structure and microhardness of Al-Ni alloy

Mechanical Performance of the Alxcocrcufeni High-Entropy Alloy System with Multiprincipal Elements

Insight into the microstructure and micromechanical behavior and mechanism of the constitutional phase of FeNiCrAl 0.63 multi-principal element alloy

Microstructure and Solidification Mode of AlTiFeNiCuCr_x High-entropy Alloy with Multi-Principal Elements

Multi-principal Element Alloys with High-density Nanotwinned 9R Phase

A Novel Martensitic-Like Transformation Fe-Based Multi-principal Element Alloy

The influences of vanadium addition and temperature on the microstructure, and mechanical properties of Al 0.1 CoCrFeNiV x multi-principal element alloys

Mechanical behaviors of novel multiple principal elements CuAl10Fe5Ni5Mn1.2 wt% with micro-nano structures

Microstructure and Mechanical Properties of Altifenicucrx High-Entropy Alloy with Multi-Principal Elements

MICROSTRUCTURE AND PROPERTIES OF CuCr25 ALLOYS WITH DIFFERENT Ni CONTENT

Theoretical and Experimental Studies of the Structural, Phase Stability and Elastic Properties of AlCrTiFeNi Multi-Principle Element Alloy

Correlation of microstructure, mechanical properties and corrosion behavior in a Ni34Co28Cr28Al10 multi-principal element alloy with outstanding corrosion resistance

Theoretical Study on Structural Stability and Elastic Properties of Fe25Cr25Ni25TixAl(25-x) Multi-Principal Element Alloys