Electrochemical Performance of Al_2O_3-coated LiMn_2O_4 Cathode Materials by Solid-state Reaction at Room Temperature

LUAN Xin-ning,HU Guo-rong,PENG Zhong-dong,DU Ke
2009-01-01
Abstract:Preparation of Al2O3-coated LiMn2O4 cathode materials by solid-state reaction at room temperature was described.The crystal structure,morphology and the electrochemical performance of the LiMn2O4 cathode materials were investigated by x-ray diffraction,scanning electron microscopy and electrochemical measurements.It is found that LiMn2O4 cathode materials have excellent cycleability by Al2O3 coating,specially at high temperature.The initial discharge capacity of the materials with 1.0wt% Al2O3-coated were 120.2 mAh/g and 117.9 mAh/g,respectively at room temperature and high temperature,among the voltage range 3.25~4.35 V at 0.5C rate,and the capacity retentions were 96.59% and 94.23% after 50 cycles,which indicated that material had high discharge capacity and good cycling property under these optimum conditions.