Abstract:In this study, the precursor precipitates of Zinc oxide (ZnO) were obtained by a direct precipitation method via the reaction between Zinc nitrate (Zn(NO3)2) and Ammonium carbonate ((NH4)2CO3) in aqueous solutions with proper concentration. X-ray diffraction (XRD) analysis demonstrated that the precursor precipitates of ZnO were Zn4(CO3)(OH)6·H2O. Both the Differential thermal analysis (DTA) and the thermal gravimetric analysis (TGA) curves of the precursor precipitates show that no further weight loss and thermal effect were observed at a temperature of above 550°C. The precursor precipitates of ZnO were subjected to thermal calcinations and finally yielded the nano-sized ZnO powders. The calcined ZnO powders were characterized by XRD, Brunauer–Emmet–Teller analysis (BET), and scanning electron microscope (SEM), respectively. The XRD results indicated that the synthesized ZnO powders had a pure wurtzite structure and the average nano-particle sizes were about 35.2nm. However, the inconsistency of ZnO particle sizes derived from the BET methods and the XRD analysis indicated that a fraction of nano-sized ZnO powders were in the form of aggregates, which was also verified by SEM and TEM image. In addition, both the SEM image and the TEM photograph demonstrated that the nano-sized ZnO particles were of a pseudo-spherical shape.

Synthesis and characterization of nano-sized ZnO powders by direct precipitation method

Preparation, Characterization and Influential Parameters of Zno Nanoparticles Synthesized by Precipitation Method

Synthesis and Characterization of ZnO Nanoparticles in the Method of Precipitation

Preparation of ZnO nanoparticles using the direct precipitation method in a membrane dispersion micro-structured reactor

Large Scale Synthesis of ZnO Nanoparticles Via Homogeneous Precipitation

Preparation of ZnO Nanoparticles Using Zinc Oxalate Dihydrate As Precursor

SYNTHESIS OF NANO-SIZED ZINC OXIDE BY PRECIPITATION METHOD AND COMBUSTION TECHNOLOGY

Preparation of nano-ZnO by direct precipitation method under ultrasonic radiation and surface modification study

Preparation of Ultrafine Zno Powder by Precipitation Method

Preparation and Characterization of Nano-Zno Flakes Prepared by Reactive Ion Exchange Method

Synthesis and Charactrization of ZnO Nanoparrticles with Different Morphology and their Structural Properties

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method

Study on the synthesis and properties of nano-ZnO

Preparation of Nanoscale CuO Powders

Preparation and Characterization of Nano-Sized ZnO Particles by Microemulsion Method

Preparation of Zno Nanoparticles by Precipitation/Mechanochemical Method

Controllable Synthesis of Highly Dispersed Zno Nanoparticles and Nanorods

SYNTHESIS OF NANOCRYSTALLINE SnO2 BY PRECIPITATION

Preparation and Characterization of Nanometer ZnO Powder

Synthesis of relatively monodisperse ZnO nanocrystals from a precursor zinc 2,4-pentanedionate

Size-Controllable Synthesis of Spherical Zno Nanoparticles: Size- and Concentration-Dependent Resonant Light Scattering