Investigation of Growth Modes of Cadmium Mercury Thiocyanate Crystal by Atomic Force Microscopy
XN Jiang,DL Sun,D Xu,DR Yuan,MK Lu,SY Guo,Q Fang
DOI: https://doi.org/10.1016/s0022-0248(01)01555-x
IF: 1.8
2001-01-01
Journal of Crystal Growth
Abstract:Growth modes on the {110} face of cadmium mercury thiocyanate CdHg(SCN)4 (CMTC) crystal as a function of supersaturation have been investigated using ex situ atomic force microscopy. The results show that in most cases growth occurs in elementary steps generated by either simple or complex screw dislocation sources. Several kinds of spiral hillocks are observed on this surface. In fact, crystal faces formed on a single hillock are very rare for the CMTC crystal. It is notable that almost all spiral hillocks are formed by the dislocation sources with components of the Burgers vectors perpendicular to the {110} crystal face of b=1 unit step height, which contribute to the absence of hollow cores at the centers of the spiral hillocks. It is also found that the structures of the dominant growth hillocks differ at the different supersaturations. On the {110} faces of CMTC crystals, 2D nucleation islands are rarely observed except at high supersaturation (σ=0.68). The 2D nuclei are circular if not deformed by the adsorption of small 3D particles. During multiple scanning on the surface, some 3D nuclei appear at the edges of 2D nuclei and gradually replace them. The new surprising fact is that at low supersaturation (σ=0.06) both 2D nuclei and spiral hillocks are imaged simultaneously on the surface, which has never been reported previously. Finally, various step morphologies are presented, in which intense roughness of steps is considered as a remarkable feature of complex compound crystals, and the formation of step bunching is described.