Editorial for Special Issue on High-Temperature Molten Salt Chemistry and Technology
Shuqiang Jiao,Mingyong Wang,Wei‐Li Song
DOI: https://doi.org/10.1007/s12613-020-2225-7
2020-01-01
Abstract:High-temperature molten salt consisting of metal cation and non-metal anion is a promising media to break the limits of aqueous solution due to high conductivity, wide electrochemical window, rapid mass transfer, high solubility to reactants, low vapor pressure, etc. In the past two hundred years, high-temperature molten salt chemistry and technology attract widely interests. Particularly, molten salt electrolysis as an indispensable metallurgy technology has been applied industrially for metal extraction of Al, rare earth, and alkali/alkaline-earth metals. It is well known that industrial aluminum electrolysis was invented by Hall and Heroult in the end of the 19th century. It is a milestone and promotes the change of Al from noble metal to bulk metal. At present, the yield of Al has reached to 62 millions tons all over the world in 2019. High-temperature molten salt chemistry and technology has brought a revolutionary advancement to human life and infrastructure construction. Since the 21st century, the application and investigation of molten salt chemistry and technology were further extended. Various novel electrolysis methods, such as FFC, OS, USTB etc., were proposed for the extraction of high melting point metals (i.e., Ti, V, Si etc.). Besides traditional metallurgy, high-temperature molten salts chemistry and technology were also used for the preparation of functional materials and the treatment of secondary resources and energy storage. High-temperature molten salt chemistry and technology have become an interdisciplinary including chemistry, physics, metallurgy, energy, environmental, and so on. It is expected to inject vitality to the development of traditional industries and will become a research hotspot. It is our honor as Guest Editors of the journal International Journal of Minerals, Metallurgy and Materials to organize the special issue on the topic of “High-temperature molten salt chemistry and technology.” It includes thirteen novel research articles and three comprehensive reviews. All papers were mainly focused on advanced electrometallurgy, recovery and utilization of secondary resources, and the preparation of functional materials and rechargeable batteries in molten salts. The original works will provide insight to understand the recent development and frontiers of high-temperature molten salt chemistry and technology. Electrometallurgy in high-temperature molten salts still receives the largest attentions. Particularly, the extraction of refractory metals and the separation of rare earth were mainly studied. FFC Cambridge Process for Ti extraction by the electrodeoxidation of solid TiO2 cathode in CaCl2 molten salts was proposed in December 1999. Generally, calcium titanate was considered as an inevitable intermediate. Wang et al. [1] used calcium titanate as solid cathode and the electrodeoxidation behavior was investigated. It was found that the reduction rate of Ca3Ti2O7 was larger than that of CaTiO3 due to more “diffusion channels” which was created by the release of Ca. Meanwhile, a new method was also proposed to convert and recycle excess CaO from Ca3Ti2O7 precursor. In addition, metal Cr was also successfully obtained by the electrodeoxidation of solid Cr2O3 cathode based on solid oxide membrane-assisted FFC Cambridge Process [2]. It was found that large porosity, small particle size, and high voltage can accelerate the reduction rate. The reduction of Cr2O3 proceeded in a two-step process, i.e. Cr2O3 to CrO, and then to Cr. Compared with aqueous electrolytes, high-temperature molten salts may lead to unwanted electrode-electrolyte interactions. Chen [3], one of inventors of FFC Cambridge Process, provided a profound review focusing on various interactions between molten salts and solid cathodes. Typical perovskitisation, non-wetting of molten salts on metals, carbon contamination to products, and the formation of oxychlorides and calcium intermetallic compounds were discussed in detail. The proper understanding to various interactions was crucial to develop the optimum and feasible