Abstract:A hybrid porous collagen scaffold mechanically reinforced with surface-activated poly(lactic acid) (PLA) fiber was prepared. PLA fibers, 20 mu m in diameter and 1 mm in length, were aminolyzed with hexanediamine to introduce free amino groups on the surfaces. After the amino groups were transferred to aldehyde groups by treatment with glutaraldehyde, different amounts (1.5, 3, 5 and 8 mg) of surface-activated PLA fibers were homogeneously mixed with 2 ml type-I collagen solution (pH 2.8, 0.6 wt%). This mixture solution was then freeze-dried and cross-linked to obtain collagen sponges with surface-activated PLA fiber. Scanning electron microscopy observation indicated that the collagen sponges had a highly interconnected porous structure with an average pore size of 170 mu m, irrespective of PLA fiber incorporation. The dispersion of surface-activated PLA fibers was homogeneous in collagen sponge, in contrast to unactivated PLA fibers. The compression modulus test results showed that, compared with unactivated PLA fibers, the surface-activated PLA fibers enhanced the resistance of collagen sponge to compression more significantly. Cytotoxicity assay by MTT test showed no cytotoxicity of these collagen sponges. L929 mouse fibroblast cell-culture studies in vitro revealed that the number of L929 cells attached to the collagen sponge with surface-activated PLA fibers, both 6 h and 24 h after seeding, was higher than that in pure collagen sponge and sponge with unactivated PLA fibers. In addition, a better distribution of cells infiltrated in collagen sponge with surface-activated PLA fibers was observed by histological staining. These results indicated that the collagen sponge reinforced with surface-activated PLA fibers is a promising biocompatible scaffold for tissue engineering. (C) Koninklijke Brill NV, Leiden, 2010

Preparation and Characterization of Collagen-Modified Polylactide Microparticles

Preparation and Cytocompatibility of Chitosan‐modified Polylactide

Collagen-coated Polylactide Microspheres As Chondrocyte Microcarriers.

Preparation of Open-Porous Stereocomplex PLA/PBAT Scaffolds and Correlation Between Their Morphology, Mechanical Behavior, and Cell Compatibility.

Reinforcement Of A Porous Collagen Scaffold With Surface-Activated Pla Fibers

Synthesis and Characterization of Collagen Type Ⅰ-modified Poly(dl-Lactic Acid) Biomimetic Material

Preparation and Properties of an Injectable Scaffold of Poly(Lactic-Co-Glycolic Acid) Microparticles/Chitosan Hydrogel

Porous Collagen Scaffold Reinforced with Surfaced Activated PLLA Nanoparticles.

Paraffin Spheres As Porogen to Fabricate Poly(L-Lactic Acid) Scaffolds with Improved Cytocompatibility for Cartilage Tissue Engineering

Hybrid Coating of Hydroxyapatite and Collagen Within Poly(d,l-Lactic-co-glycolic Acid) Scaffold.

A Novel Poly (Lactic-Co-Glycolic Acid)-Collagen Hybrid Scaffold Fabricated Via Multi-Nozzle Low-Temperature Deposition

Enhancing the Cytocompatibility of Poly(D,L-lactide) by a Plasma Technique and Coupling Collagen

Characterization on Modification and Biocompatibility of PCL Scaffold Prepared with Near-field Direct-writing Melt Electrospinning

Ultrasound-mediated Preparation and Evaluation of a Collagen/pvp-Pcl Micro- and Nanofiber Scaffold Electrospun from Chloroform/ethanol Mixture

Fabrication and Biocompatibility of Cell Scaffolds of Poly(l-Lactic Acid) and Poly(l-Lactic-co-glycolic Acid)

Preparation and Characterization of Microporous Poly(d,l-Lactic Acid) Film for Tissue Engineering Scaffold

Cartilage Tissue Engineering PLLA Scaffold with Surface Immobilized Collagen and Basic Fibroblast Growth Factor

Preparation and Characterization of Polylactide/poly(ε-Caprolactone)-poly(ethylene Glycol)-Poly(ε-caprolactone) Hybrid Fibers for Potential Application in Bone Tissue Engineering.

Investigation of Plasma Treatment and Collagen Immobilization on the Surface of Poly(lactid-glycolide Acid)

Fabrication of composition-graded collagen/chitosan–polylactide scaffolds with gradient architecture and properties

Optimization and characterization of chemically modified polymer microspheres and their effect on cell behavior