THE INFLUENCES OF NANOCLAY ON VISCOELASTIC RESPONSE OF LOW DENSITY POLYETHYLENE MELTS UNDER SHEAR

Yang Hongmei,Zhang Zhenwei,Zheng Qiang

DOI: https://doi.org/10.3724/sp.j.1105.2007.00705

2009-01-01

Abstract:The viscoelastic responses for the melts of low density polyethylene(LDPE)/ethylene-vinyl acetate copolymer(EVA)/nanoclay composites containing different contents of nanoclay were studied.It is found that the viscoelasticity dependence of the melts on shear rate,shear strain and shear history is related with the dispersion and amount of nanoclay added.A negative primary normal force difference(N-1) appears when the composites are sheared at lower shear rate during steady flow,while N-1 is independent of the nanoclay amount at higher shear rates.Moreover,compared with the polymer matrix,the composites exhibit different dependence of transient stress or N-1 on the strain.The viscoelastic responses of polymer matrix are independent of the pre-shear that the samples are exposed to.However,for the composites containing 3 wt% or more nanoclay,the level of transient stress,stress overshoot and the steady stress observed in flow reversal experiments with pre-shear are found to be lower than those of the samples without pre-shear.With the increasing of nanoclay content,the differences of transient stress at steady state increase for the composites with and without pre-shear,and a positive N-1 instead of a negative one appears for the composites subjected to pre-shear.It is believed that the layers of nanoclay are exfoliated or intercalated by polymer chains,resulting in the formation of directors in the polymer matrix.The reason for the composites melts showing abnormal nonlinear viscoelastic response is ascribed to alignment or orientation of the directors under shear stress.