Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Preparation and Characterization of Mn DopedZnO Nanofibers

Zn-doped SnO2 Nanoparticles: Structural, Optical, Dielectric and Magnetic Properties

Preparation of ZnS Nanofibers Via Electrospinning

Fabrication and Magnetic Property of Mn Doped ZnO Nanowires

LaMnO3 and La0.875Sr0.125MnO3 Nanofibers via Electrospinning

LaMnO_3 and La_(0.875)Sr_(0.125)MnO_3 Nanofibers via Electrospinning

Electronic Structure and Magnetism of Mn-Doped ZnO Nanowires

Preparation of Manganese-Doped Znse Precursor Nanoribbon Bundles and Investigation of Its Magneto-Optical Properties

Preparation of Eu, Li co-doped ZnO red fluorescence nanofibers by electrospinning and their characterization

Exciton quenching and ferromagnetism-to-ferrimagnetism crossover in diluted magnetic semiconducting Zn1-xCoxO nanogranular nanofibers

Fabrication And Characterization Of Single-Crystalline Nanostructured Zn1-Xmnxs

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Fabrication of Mn2O3 Nanowire with Ultra Fine Morphology Via an Electrospinning Technology

Synthesis, Characterization and Magnetic Property Measurements of Zn1-Xmnxo Nanoparticles Via Vapour Phase Growth

Characterization of Mn-doped ZnO Nanobelts by Electron Energy-Loss Spectroscopy

Synthesis and Characterization of Y and Mn -Doped ZnO Nanoparticles: Structural, Optical, Morphological, and Gas Sensing Investigations

Synthesis of Co‐Doped ZnO Nanofibers and Their Magnetic Properties

Preparation and Characterization of Sc2o3-Doped Zro2 Nanofiber

Microwave-assisted preparation and in vitro characterizations of doped superparamagnetic ferrite nanoclusters

Ferromagnetic and Optical Behaviors Observed in Mn-Doped Zno-Based Thin Films

Paramagnetic nature of Mn doped ZnS nano particles in opto electronic device application