Abstract:Small-diameter metallic single-wall carbon nanotubes (SWNT) were separated from larger diameter semiconducting SWNT when CoMoCAT samples (supplied with abundance of (6,5) species) were left standing at ambient laboratory condition for a few days in dimethylformamide solution containing ethylanthraquinone (EAQ). SWNT enriched in larger diameter semiconducting species by this method were used to fabricate SWNT network-based thin film transistors (TFTs). The resulting devices had mobilities of 0.2 cm(2)/(V s) and on/off ratios of about 10(4). The on/off ratios were greatly improved, by approximately 2 orders of magnitude, over those of TFTs made with pristine SWNT. The enrichment in semiconducting tubes was corroborated by UV-vis-NIR absorption, photoluminescence excitation (PLE), and resonance Raman scattering spectroscopy. Density functional simulations show that hydroxyl radicals preferentially attack small-diameter metallic and then small-diameter semiconducting nanotubes over larger diameter semiconducting tubes. We propose that EAQ forms radicals in ambient lighted conditions, resulting in this diameter-and metallicity-selective reaction which increases the density of the target species, promoting their sedimentation under centrifugation. This simple method of obtaining semiconducting-enriched SWNT samples should be widely applicable for printed electronic devices.

Extraction of Metallic Nanotubes of Zeolite-Supported Single-Walled Carbon Nanotubes Synthesized from Alcohol

Synthesis of Carbon Nanotubes by Decomposing Alcohol

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Direct Enrichment Of Metallic Single-Waited Carbon Nanotubes Induced By The Different Molecular Composition Of Monohydroxy Alcohol Homologues

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

Large-scale Separation of Metallic and Semiconducting Single-Walled Carbon Nanotubes.

Carbon Nanotubes Synthesized By Rapid Quenching Of Red-Hot Graphite Rod In Ethyl Alcohol

Purification and Characterization of Single-Walled Carbon Nanotubes Synthesized by Chemical Vapor Deposition

The influence of ethanol on the growth and structure of carbon nanotubes

Selective Synthesis Combined with Chemical Separation of Single-Walled Carbon Nanotubes for Chirality Selection

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Separation of Metallic Single‐walled Carbon Nanotubes Using Various Amines

Selective Small-Diameter Metallic Single-Walled Carbon Nanotube Removal by Mere Standing with Anthraquinone and Application to a Field-Effect Transistor

Single-walled carbon nanotubes: synthesis and quantitative purification evaluation by acid/base treatment for high carbon impurity elimination

Dispersion and Separation of Small-Diameter Single-Walled Carbon Nanotubes

Why semiconducting single-walled carbon nanotubes are separated from their metallic counterparts.

Why Semiconducting Single-Watted Carbon Nanotubes Are Separated From Their Metaltic Counterparts

Simple Purification and Selective Enrichment of Metallic SWCNTs Produced Using the Arc-Discharge Method

Fabrication of Single-Walled Carbon-Nanotube with Metallic Electrodes

Large- Scale Production of Single- Walled Carbon Nanotubes Using Fe/Mo/MgO Cryogel Catalyst