Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Synthesis of Ni Nanowires Via a Hydrazine Reduction Route in Aqueous Ethanol Solutions Assisted by External Magnetic Fields

Facile and rapid synthesis of nickel nanowires and their magnetic properties

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Electrochemical fabrication and structure of Ni<sub><i>x</i></sub>Zn<sub>1−<i>x</i></sub> alloy nanowires

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Facile Synthesis of Bimetallic Ag/Ni Core/sheath Nanowires and Their Magnetic and Electrical Properties.

Electrospinning Of Fe, Co, And Ni Nanofibers: Synthesis, Assembly, And Magnetic Properties

Controlled Synthesis and Magnetic Properties of Ni Nanotubes and Nanowires

Experimental and Micromagnetics Studies on Magnetism of Ni Nanowire Arrays Prepared with Magnetic Field Induction

Magnetic-field-induced Rapid Synthesis of Defect-Enriched Ni-Co Nanowire Membrane As Highly Efficient Hydrogen Evolution Electrocatalyst

Fabrication of One-Dimensional Magnetic Particles Chain of Polycrystalline Nickel under Magnetic Field

Synthesis of Ni Nanochains with Various Sizes: the Magnetic and Catalytic Properties

Diameter-Controlled Synthesis of Polycrystalline Nickel Nanowires and Their Size Dependent Magnetic Properties

Structural, magnetic, and magnetoresistive properties of electrodeposited Ni5Zn21 alloy nanowires.

Fabrication of monodispersed nickel flower-like architectures via a solvent-thermal process and analysis of their magnetic and electromagnetic properties

Zn-doped Ni nanotubes prepared by the chemical reduction method in ethanol solution

Magnetic field-induced solvothermal synthesis of one-dimensional assemblies of Ni-Co alloy microstructures

Structural, Magnetic, and Magnetoresistive Properties of Electrodeposited Ni<sub>5</sub>Zn<sub>21</sub>Alloy Nanowires

Electrochemical Fabrication And Structure Of Nixzn1-X Alloy Nanowires

Room temperature synthesis and one-dimensional self-assembly of interlaced Ni nanodiscs under magnetic field

Magnetic field assisting DC electrodeposition: general methods for high-performance Ni nanowire array fabrication.