Effect of Lanthanum/Aluminum-modified zeolite on phosphorus removal from eutrophic water
MENG Shunlong,HU Gengdong,QU Jianhong,LI Yongdan,ZHANG Tian,CHEN Jiazhang,XU Pao
DOI: https://doi.org/10.3969/j.issn.1674-5906.2012.11.018
2012-01-01
Abstract:Phosphorus is a very important element in water contamination.Excess discharge of phosphorus into water often causes eutrophication,and results in deterioration of water quality.The presence of trace concentration of dissolved phosphate in the treated wastewater from municipalities and industries is often responsible for causing eutrophication problems.Water pollution by phosphorus is increasing,and therefore there is an increasing demand for removal of phosphorus.Solid adsorption has been used widely in purifying waste water,and it has good effect on decreasing phosphorus when the phosphorus concentration of waste water is high,however,it has no effect on decreasing phosphorus when the phosphorus concentration of waste water is lower than 0.5 mg.L-1.Unfortunately,for the phosphorus concentration in eutrophic water is always lower than 0.5 mg.L-1,so there are some bottle-neck problem about the application of solid adsorption in purifying eutrophic water.In order to solve the bottle-neck problem and promote the application of solid adsorption in purifying eutrophic water,the phosphorus adsorption characteristics of Lanthanum/Aluminum-modified zeolite and its phosphorus adsorption capability on the eutrophic water were researched in the experiment.And the Lanthanum/Aluminum-modified zeolite used in the experiment was made of LaCl3,AlCl3and zeolite and by the technics flow of confecting metal ion solution,confecting precipitator solution,deposition reaction and calcination.The results showed that Lanthanum/Aluminum-modified zeolite had effective phosphorus removal capability both on higher and lower phosphorus concentration wastewater.The phosphorus adsorption reached equilibrium after 36 h at the temperature of 30 ℃,and the saturation adsorption amount was 2.44 mg.g-1.When the dosage of Lanthanum/Aluminum-modified zeolite was 8 g.L-1,the phosphorus in wastewater could decrease from 20 mg.L-1 to 0.515 mg.L-1 and the removal ratio was as high as 97.43%.The adsorption of phosphorus onto Lanthanum/Aluminum-modified zeolite increased with an increase of contact time.The adsorption process can be divided into two steps: a rapid initial adsorption(3 h) and a much slower subsequent adsorption process.During the rapid initial adsorption(3 h) period,the removal ratio and adsorption amount were 57.1% and 1.43 mg.g-1 respectively,and the adsorption amount accounted for 58.6% of the saturation adsorption amount.The results of Lanthanum/Aluminum-modified zeolite on phosphorus removal from eutrophic water showed that the concentrations of phosphorus in eutrophic lake water and eutrophic pond water were under the lowest detection limit(0.01 mg.L-1) after two times of filtration and three times of filtration respectively,which showed Lanthanum/Aluminum-modified zeolite has good effect on phosphorus removal from low phosphorus concentration waste water.Lanthanum/Aluminum-modified zeolite had effective phosphorus removal capability on lake water adding with phosphorus.However,the saturation adsorption amount(2.02 mg.g-1) of Lanthanum/Aluminum-modified zeolite on the lake water adding with phosphorus was lower than that on man-made wastewater,which meant that the coexisting ions in natural wastewater could decrease the phosphorus adsorption capability of Lanthanum/Aluminum-modified zeolite.