Abstract:MgNi-based alloys have been regarded as very promising anode material for nickel-metal hydride battery owing to their electrochemcial capacity much higher than that of AB(5) alloys. However, Mg-Ni alloy anodes generally suffer very serious capacity decay in cycling, which is previously ascribed to the corrosion of Mg in alkali electrolyte in the past decades. To further reveal the capacity fading mechanism of MgNi-based alloys, the electrochemcial hydrogen storage properties of Mg2Ni and amorphous Mg50Ni50 alloys and their microstructural evolution during cycling were comparatively studied. It has been firstly demonstrated that it is the amorphous MgNi phase instead of Mg2Ni phase contributes to electrochemical discharge capacity, because the Mg2NiH4 hardly released hydrogen under electrochemcial conditions. Then, it has been found that the charge input level has significant effect on the cyclic performance of amorphous Mg50Ni50 alloy anode. At full charge of 500 mAh g(-1), the amorphous MgNi phase easily crystallized to the nanocrystalline Mg2NiH4, which leaded to the capacity decay immediately. Comparatively, with the low charge input of 100 mAh g(-1), the discharge capacity of amorphous Mg50Ni50 alloy remained almost unchanged for 425 cycles. The excellent cyclability is attributed to the less hydrogenation-induced crystallization at low charge input. This work clearly demonstrates that the hydrogenation-induced crystallization is a dominating reason for the electrochemical capacity decay in the milled amorphous Mg-Ni anode. It provides a new approach to improve the electrochemcial properties of Mg-Ni alloy electrode by inhibiting the hydrogenation-induced crystallization. (C) 2019 Elsevier Ltd. All rights reserved.

Formation of Hydrogen Blister on AZ91 Magnesium Alloy During Cathodic Charging

States and Transport of Hydrogen in the Corrosion Process of an Az91 Magnesium Alloy in Aqueous Solution

Effect of Electrochemical Hydrogen Charging on Blistering and Mechanical Properties Behavior of Q690 Steel

ESEM Observation of the Process of Hydrogen Generation Around the Micro-Droplets Forming on AZ91 Magnesium Alloy

Electrochemical Corrosion and Mechanical Behaviors of the Charged Magnesium

An electrochemical investigation of mechanical alloying of MgNi-based hydrogen storage alloys

Effect of Magnesium Hydride on the Corrosion Behavior of an AZ91 Magnesium Alloy in Sodium Chloride Solution

Effect of Hydrogen on Corrosion and Stress Corrosion Cracking of AZ91 Alloy in Aqueous Solutions

Effect of electrochemical hydrogen charging on the microstructure and mechanical behavior of a duplex structured Mg-8wt.%Li alloy

The Corrosion Behavior of AZ91D Magnesium Alloy in Simulated Haze Aqueous Solution

Electrolytic hydrogen charging,annealing and mechanical properties of ZL114 alloy

Investigation of Stress Corrosion Cracking Behaviors of an AZ91 Magnesium Alloy in 0.1 Kmol/m 3 Na2SO4 Solution Using Slow Strain Rate Test

Hydrogenation and Crystallization of Amorphous Phase: A New Mechanism for the Electrochemical Capacity and Its Decay in Milled Mg-Ni Alloys

Effect of hydrogen charging time on hydrogen blister and hydrogen-induced cracking of pure iron

Effect of microstructure on the hydrogenation behavior of AZ61 magnesium alloy with silicon carbide and nickel additives, processed by equal channel angular pressing

Revealing the Influence of Solution and Pre-Deformation Treatment on the Corrosion Resistance of Y-modified AZ91 Magnesium Alloy for Lithium-Ion Battery Shell

Electrochemical Investigations on AZ Series Magnesium Alloys as Anode Materials in a Sodium Chloride Solution

Effects of Hydrogen on the Anodic Behavior of Alloy 690 at 60 °C

Microstructural Investigation of Electrochemical Hydrogen Storage in Amorphous Mg–Ni–La Alloy

Study on the Anodic Film Formation Process of AZ91D Magnesium Alloy

Effect of Hydrogen on Stress Corrosion Cracking of Magnesium Alloy in 0.1M Na2SO4 Solution