Molecular Weight and Particle Size Distribution of Latex in the Process of Emulsion Polymerization for Styrene Butadiene Rubber with High Monomer Conversion

JIN Yan-jiang,SHEN Ben-xian,SUI Jun,CUI Ming-hai,YANG Lei,ZHAO Ji-gang

DOI: https://doi.org/10.3969/j.issn.1005-3174.2011.04.009

2011-01-01

Abstract:The monomer conversion of styrene butadiene rubber polymerization was studied by a lab scale autocalve with the large-scale production recipe of high conversion for styrene butadiene rubber in Jilin Petrochemical Company.The molecular weight and particle size distributions of latex in the process of emulsion polymerization for styrene butadiene rubber with high monomer conversion were determined by laser particle size analyzer and gel permeation chromatography.The results showed that:the particle size distribution of latex is Gaussian distribution.The particle size is mainly in the vicinity of 0.1 microns,the average particle size of latex increases with increasing polymerization time,while the increasing rate is less and less.When the polymerization time was less than 11 hours(the monomer conversion was less than 72%),the weight average molecular weight and Z average molecular weight of latex increased with increasing the polymerization time.The molecular weight distribution breadth index decreases with increasing the reaction time.It indicated that the styrene butadiene rubber by high conversion recipe by adjusted can effectively improve the polymerization of the latex particle size distribution.