Abstract:This paper reports the development of TiCN - Co - Cr3C2 - Si3N4 cermets modified with the addition of B4C. Cermets of three different compositions with varying B4C in TiCN - Co - Cr3C2 - Si3N4 were fabricated. The TiCN, Co, Cr3C2, Si3N4 and B4C powders in the combinations 80%TiCN-5%Co-5%Cr3C2–5%Si3N4–5%B4C; 75%TiCN-5%Co-5%Cr3C2–5%Si3N4–10%B4C; 70%TiCN-5%Co-5%Cr3C2–5%Si3N4–15%B4C were ground in a ball milling unit for six hours at a speed of 300 rpm at a ball-to-powder ratio of 10:1. The powders were then sintered in a vacuum hot press at a temperature of 1600 °C and a pressure of 50 MPa with soaking time of 90 min. For comparison purpose, 90%TiCN-5%Co-5%Cr3C2 cermet was prepared. The microstructure of the sintered cermets revealed the core-rim structure. The Vickers hardness test was done with a load of 10 Kg and for duration of 10 s. Fracture toughness was measured using the crack length data obtained from the hardness test using scanning electron microscopy. The cermet with a composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C produced higher hardness of 26.53 ± 0.56 GPa and fracture toughness of 10.29 ± 0.18 MPa m and 70% TiCN-5%Co-5% Cr3C2–5% Si3N4–15% B4C showed high fracture toughness value of 11.23 ± 0.09 MPa m with hardness value of 21.05 ± 0.10 GPa. The cermet composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C retained the hardness of 16.85 GPa even after annealing at 600 °C. The sintered cermets tend to form TiO2 which determines the hardness of the annealed cermets at a range of 600 °C – 1000 °C. The presence of these oxides tends to decrease the hardness. The wear test was performed taking the cermet as the pin material. The abrasive and adhesive wear mechanisms were dominant in the cermets. The harder precipitates formed tend to increase wear resistance by reducing the wear rate. The harder precipitates (TiN and TiB2) formed mainly due to the addition of Si3N4 and B4C, this addition promotes adhesive wear by a tribolayer formation.

Effect of Boronizing on Microstructure and Properties of Ti（ C, N）-based Cermet

Effect of Boronizing on Thermal Shock Resistance of Ti( C, N)-based Cermet

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Formation and Kinds of Boride on Microstructure Evolution and Mechanical Properties in Ti47.5Al2.0Cr2.0NbxB Alloys

Strengthening and toughening of Ti(C,N)-based cermets: (Ti,W)C additive design and the mechanism

Microstructure, mechanical properties, and corrosion resistance of Mo2(Fe,Ni)B2-based cermets prepared by reaction boronizing sintering

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF NANO MODIFIED CERMETS

Microstructure and mechanical properties of newly synthesized Mo(Co,Fe)B cermets

Effect of Boron Addition on Microstructure, Mechanical Properties and Oxidation Resistance of TaC Ceramics

Effect of Tic/Tin Powder Size on Microstructure and Properties of Ti(C, N)-Based Cermets

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Effects of Carbon and Boron Addition on Microstructure and Mechanical Properties of TiAl Alloys

Effects of Ti on the Microstructural Evolution and Mechanical Property of the SiBCN-Ti Composite Ceramics

Effects of Boron on Microstructure Evolution and Mechanical Properties in Ti46Al8Nb2.6C0.8Ta Alloys

Synthesis of TiB 2 /Ti(C,N) cermet by RSPS: formation mechanism, shrinkage behavior, and mechanical properties

On the effects of B4C addition on the microstructure, mechanical properties, wear and thermal stability of TiCN- co -Cr3C2-Si3N4 cermets developed by vacuum hot pressing

Preparation and Properties of Titanium Diboride Ceramic Matrix Reinforced by Carbon Nanotubes

Effect of Nano-Si3n4 Addition on the Microstructure and Mechanical Properties of Ticn-Based Cermets

Effects Of Mechanical Ball Milling Time On The Microstructure And Mechanical Properties Of Mo2nib2-Ni Cermets

Effect of synthetic Mo2FeB2 powder on the microstructure and mechanical properties of Mo2FeB2-based cermets