Preparation and Characterization of Carbon Membranes Made from Poly(phthalazinone Ether Sulfone Ketone)

Bing Zhang,Tonghua Wang,Shouhai Zhang,Jieshan Qiu,Xigao Han

DOI: https://doi.org/10.1016/j.carbon.2006.03.039

IF: 10.9

2006-01-01

Carbon

Abstract:Carbon membranes were prepared from a novel polymeric precursor of poly(phthalazinone ether sulfone ketone) (PPESK), of which the changes of microstructure and chemical compositions during pyrolysis from 500°C to 950°C were monitored by thermal gravimetric analysis, X-ray diffraction, X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy. It has been found that the weight loss of the PPESK precursor up to 800°C is about 43.0wt%. After the heat treatment, the typical chemical structure of the PPESK precursor disappears, at the same time a graphite-like structure with more aromatic rings is formed. The interlayer spacing (i.e., d value) decreases from 0.471nm to 0.365nm as the pyrolysis temperature increases. The gas permeation performance of carbon membranes has been tested using pure single gases including H2, CO2, O2 and N2. For the carbon membrane obtained by carbonizing the PPESK precursor at 800°C, the maximum ideal permselectivities for H2/N2, CO2/N2 and O2/N2 gas pairs could reach 278.5, 213.8 and 27.5, respectively.