Abstract:The ordered mesoporous silica MCM-48 with cubic Ia3d structure was synthesized using the cationic surfactant hexadecyltrimethylammonium bromide (CTAB) as a template agent and tetraethylorthosilicate (TEOS) as a silica source. The obtained material was first functionalized with (3-glycidyloxypropyl)trimethoxysilane (KH560); further, two types of amination reagents were used: ethylene diamine (N2) and diethylene triamine (N3). The modified amino-functionalized materials were characterized by powder X-ray diffraction (XRD) at low angles, infrared spectroscopy (FT-IR) and nitrogen adsorption-desorption experiments at 77 K. Characterization from a structural point of view reveals that the ordered MCM-48 mesoporous silica has a highly ordered structure and a large surface area (1466.059 m2/g) and pore volume (0.802 cm3/g). The amino-functionalized MCM-48 molecular sieves were tested for CO2 adsorption-desorption properties at different temperatures using thermal program desorption (TPD). Promising results for CO2 adsorption capacities were achieved for MCM-48 sil KH560-N3 at 30 °C. At 30 °C, the MCM-48 sil KH560-N3 sample has an adsorption capacity of 3.17 mmol CO2/g SiO2, and an efficiency of amino groups of 0.58 mmol CO2/mmolNH2. After nine adsorption-desorption cycles, the results suggest that the performance of the MCM-48 sil KH N2 and MCM-48 sil KH N3 adsorbents is relatively stable, presenting a low decrease in the adsorption capacity. The results reported in this paper for the investigated amino-functionalized molecular sieves as absorbents for CO2 can be considered as promising.

Amine-functionalized mesoporous silica for CO2 and N2 separation by PSA

Preparation and Co2 Sorption/Desorption of N-(3-Aminopropyl) Aminoethyl Tributylphosphonium Amino Acid Salt Ionic Liquids Supported into Porous Silica Particles

Synthesis and CO2 adsorption property of amino-functionalized silica nanospheres with centrosymmetric radial mesopores

Improvement of Adsorbent Materials for CO 2 Capture by Amine Functionalized Mesoporous Silica with Worm-Hole Framework Structure

An Immobilized Amine with Improved Cyclic Performance Prepared from Carboxyl Modified Mesoporous Silica for CO2 Capture

CO2 capture of three-dimensional worm-hole mesoporous silica

CO2 Capture by the Amine-modified Mesoporous Materials

Amine Immobilized Three-Dimensional Worm-Hole Mesostructured MSU-J Silica for CO2 Adsorption:Effect of Amine Loading and Temperature on the Adsorption Capacity

Flexible, amine-modified silica aerogel with enhanced carbon dioxide capture performance

Synthesis and CO2 Adsorption Performance of Amine loaded Silica Aerogel

Development of amine-pillar[5]arene modified porous silica for CO2 adsorption, and CO2/CH4, CO2/N2 separation

CO2 Adsorption by Polyamine-Based Protic Ionic Liquid-Functionalized Mesoporous Silica: Regenerability and Influence of Flue Gas Contaminants

Pentaethylenehexamine-Loaded Hierarchically Porous Silica for CO2 Adsorption

Adsorption separation of CO_2 from flue gas by hyperbranched solid-amine

Amine-functionalized Mesoporous Silica Derived from Natural Phyllosilicate for Efficient CO2 Adsorption

Utilizing silica fume and synthetically produced mesoporous silicas for simulated flue gas CO2 adsorption

Functionalized Ordered Mesoporous MCM-48 Silica: Synthesis, Characterization and Adsorbent for CO2 Capture

Enhanced CO2 Adsorption Property of Amine In-Situ Hybrid SiO2 Aerogels by the Incorporation of Micropores

Facile Co-Precursor Sol-Gel Synthesis of a Novel Amine-Modified Silica Aerogel for High Efficiency Carbon Dioxide Capture.

Facile fabrication of mesoporosity silica as support for solid amine CO2 adsorbents with enhanced adsorption capacity and kinetics

The Influence of Pore Size and Pore Structure of Silica-Based Material on the Amine-Modified Adsorbent for CO2 Capture