Abstract:In this study, we propose a novel approach to toughening polypropylene (PP) by integrating in-situ fibrillation technology with the silane crosslinking mechanism. Specifically, we graft vinyl trimethoxy silane (VTMS) onto the backbone of ethylene-butene-rubber (EBR) chains using reactive extrusion . Subsequently, we perform the in-situ fibrillation process using a spunbond machine, resulting in PP composites with in-situ nano-fibrillated EBR-g-VTMS. The next step involves crosslinking the fibrillated EBR-g-VTMS using moisture in order to preserve the fibrillar morphology. The unique fibrillar morphology and the substantial interfacial area of the rubber phase significantly enhance the mechanical, rheological, and crystallization behavior of the PP composites. Rheological data reveal that the in-situ nano-fibrillated rubber phase forms an interconnected network at around 3 wt% loading. Scanning Electron Microscopy (SEM) images show that the average EBR-g-VTMS fiber size is approximately 70–80 nm at 10 wt% rubber loading. Notably, the presence of fibrillar EBR-g-VTMS leads to a substantial increase in β phase content up to ∼65 %. Moreover, the matrix-spanning network of cross-linked EBR fibers exhibits toughening mechanisms superior to those found in classical sea-island blends, resulting in a dramatic enhancement of PP toughness across various test conditions (such as 50 % in the elongation at break in room temperature, 300 % in sub-zero tensile testing , and 200 % in Izod impact test) while showing only marginal reduction around 10 % in its strength and stiffness. Finally, this innovative and practical approach enables the leveraging of in-situ fibrillation for a wide range of polymer/rubber systems, optimizing rubber performance as a toughening agent.

Irradiation-Induced Surface Graft Polymerization Onto Calcium Carbonate Nanoparticles and Its Toughening Effects on Polypropylene Composites

Investigations on Nano-CaCO3 Reinforced and Toughening Polypropylene/Elastomer Composites

Atomic force microscopy study on structure and properties of irradiation grafted silica particles in polypropylene-based nanocomposites

Synthesis of ACR/nanometer SiO2 Composite Particles and Their Tonghening Effect on PVC

Irradiation Initiated Grafting of Poly(Butyl Acrylate) Onto Nano-Sized Calcium Carbonate Particles

GRAFTING POLYMERIZATION ONTO NANOSILICA AND ITS EFFECT ON MECHANICAL PROPERTIES OF PP COMPOSITES

Structure–property relationships of irradiation grafted nano-inorganic particle filled polypropylene composites

Interfacial Effects in Polypropylene–silica Nanocomposites

Interfacial enhancement of nano-SiO2/polypropylene composites

Effects of the Reinforcement and Toughening of Acrylate Resin/Caco3 Nanoparticles on Rigid Poly(Vinyl Chloride)

Silica Hybrid Particles with Nanometre Polymer Shells and Their Influence on the Toughening of Polypropylene.

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Synergistic effects of toughening of nano-CaCO3 and toughness of β-polypropylene

Tensile Properties of Polypropylene Filled with Nanoscale Calcium Carbonate Particles

Performance Improvement of Polymers by the Addition of Grafted Nano-Inorganic Particles

Preparation of Nano-Silica/Polypropylene Composites Using Reactive Compatibilization

Tensile Performance Improvement of Low Nanoparticles Filled-Polypropylene Composites

Effect of grafted polymeric foaming agent on the structure and properties of nano-silica/polypropylene composites

Effect of Wet Surface Treated Nano-Sio2 on Mechanical Properties of Polypropylene Composite

Performance Improvement of Nano-silica/Polypropylene Composites Through In-Situ Graft Modification of Nanoparticles During Melt Compounding

Fabricating super-tough polypropylene nanocomposites incorporating silane cross-linked in-situ nano-fibrillated ethylene-1-butene copolymer