Preparation of Macro-Scale Spindle Polystyrene Particles by Suspension Polymerization and Their Formation Mechanism

Dong Chen,Yu-hong Ma,Yan Shi,Wan-tai Yang

DOI: https://doi.org/10.3724/sp.j.1105.2013.13006

2013-01-01

Acta Polymerica Sinica

Abstract:Poly(styrene-alt-maleic anhydride) (SMA) was prepared by solution polymerization of styrene(St) and (MAH). SMA was saponified with KOH to get SMAA, and the resulting SMAA then served as polymeric surfactant for the suspension polymerization of St. The influence of ionization degree of SMAA, rotation speed and weight ratio of St to water on the size and morphology of the obtained PS particles has been studied in detail by optical microscopy and SEM. When ionization degree of the SMAA was 50%,the SMAA was partially saponified product containing both carboxylic acid and carboxylate groups. By using this SMAA as polymeric surfactant, spindle PS particles were prepared at high ratios of St to water(3.0:3.5 similar to 3.0:4.5) and medium rotation speeds. At optimum reaction conditions, the average size of the particles was 6.8 mm in length, 1.4 mm in width,0.5 mm in thickness and the ratio of length to width was 5.0. With increasing rotation speed, the size of the particles decreased gradually and the ratio of length to width became higher. Based on these experiment results, the formation mechanism of the PS nonspherical particles by suspension polymerization in the presence of SMAA was preliminarily proposed.