Morphology Development Of Ultrathin Symmetric Diblock Copolymer Film Via Solvent Vapor Treatment
Xuan Yu,Juan Peng,Liang Cui,Hanfu Wang,Binyao Li,Yanchun Han
DOI: https://doi.org/10.1021/ma0497761
IF: 5.5
2004-01-01
Macromolecules
Abstract:We have followed the time development of the microdomain structure in symmetric diblock copolymer poly(styrene-b-methyl methacrylate), P(S-b-MMA), ultrathin films via PMMA-selective solvent vapor treatment by atomic force microscopy (AFM). After preparation on a substrate preferentially attracting the PMMA block, PS forms a continuous layer at a film's free surface. With subsequent solvent vapor treatment, the film gradually shows a well-ordered hexagonally packed nanocylinders structure. It is shown that only when the film thickness is less than the 1/2L(0) (lamellar repeat spacing), and exposed to PMMA block selective solvent for an appropriate time, can the well-ordered hexagonally packed nanocylinders form. On an extended solvent vapor treatment, a mixed morphology containing nanocylinders and stripes appears, followed by the striped morphologies. When the annealing time is long enough, the film comes back to the flat surface again, however, with PMMA instead of PS dominating the free surface. Thickness confinement and solvent induced reconstruction of the film are shown to be responsible for the P(S-b-MMA) morphology and surface chemistry development.