Influences of Nano-Si02 on Property of PPO/BCE Composites

WANG Qian-qian,YAN Hong-xia,WANG Yan-li,TANG Yu-sheng

DOI: https://doi.org/10.3969/j.issn.1004-2849.2011.03.004

2011-01-01

Abstract:With BCE(bisphenol A cyanate ester) modified by polyphenylene oxide resin(PPO) as matrix resin of composite,nano-SiO2 filler treated by silane coupler(KH-560) as modifier,so a nano-SiO2/PPO/BCE composite was prepared.The results showed that the toughness and strength can be synchronously enhanced,and the dielectric property and moisture absorption can also be improved for PPO/BCE system when nano-SiO2 content was appropriate.The impact strength(19.6 kJ/m2) or flexural strength(116.8 MPa) of nano-SiO2/PPO/BCE composite were 33.3% or 3.85% more than those of pure PPO/BCE system,but the water absorptions between nano-SiO2/PPO/BCE composite and pure PPO/BCE system were similar,and the dielectric constant of nano-SiO2/PPO/BCE composite was more than that of pure PPO/BCE system,but the dielectric loss factor of nano-SiO2/PPO/BCE composite was less than that of pure PPO/BCE system when mass fraction of nano-SiO2 was 3%.