Residual Stress Analysis of Micro-Arc Oxidation Coatings Prepared on Magnesium Alloy Substrate at Different Duration

顾艳红,蔡晓君,宁成云,熊文名,张建军,赵杰

DOI: https://doi.org/10.16577/j.cnki.42-1215/tb.2013.04.015

2013-01-01

Abstract:Sodium phosphate solution was adopted as the electrolyte to prepare a series of micro-arc oxidation(MAO) coatings on AZ31 magnesium alloy substrate while the potential was adjusted as 325 V and the micro-arc oxidation duration was adjusted as 1,3,5,8 min.The microstructure of as-prepared MAO coatings was observed with a scanning electron microscope,and an X-ray diffractometer was performed to determine their phase composition and residual stress.Moreover,potentiodynamic polarization test was combined with calculation by Stoney equation to determine the porosity of as-prepared MAO coatings.It was found that the four kinds of as-prepared MAO coatings were all dominated by compressive residual stress in a range of 194～652 MPa.Particularly,the MAO coating obtained after 5 min of micro-arc oxidation was the most compact and had the minimum porosity and residual stress,which was confirmed by relevant calculations based on Stoney equation.This meant that Stoney equation could be well adopted to estimate the effect of micro-arc oxidation duration on the resi dual stress of MAO coatings on Mg alloy substrate.