Abstract:Polystyrene colloidal template was prepared by evaporation deposition method with as-prepared polystyrene microspheres with the size of 340+/-10nm as raw material and inverse opal zirconia was fabricated by colloidal crystal-templating method. The optimal process of preparation of polystyrene colloidal template and inverse opal zirconia were deeply studied via orthogonal experiment design and range date processing. The factors, which affect the morphology of polystyrene template and inverse opal zirconia, and the corresponding values were considered, respectively and the primary and secondary order of factors were also determined. The results showed that the optimal process of preparation of polystyrene colloidal template was that self-assembly temperature was 55 degrees C, emulsion height was 1.5 cm, emulsion consistence kept 4.0% and container diameter was Phi 6.0 cm. It also found that the as-prepared polystyrene template showed bright green color and the better polystyrene template structure was, the brighter green color can be obtained. The optimal process of preparation of inverse opal zirconia was that impregnation time was once, mass ratio of polystyrene template and precursor kept 1 : 15, precursor ratio of zirconium acetate and methanol kept 1 : 1 and calcination temperature was 450 degrees C.

Preparation and Characterization of Pb0.56Sr0.44Zr0.52Ti0.48O3 Inverse Opal

Photonic Band Gap In (Pb,La)(Zr,Ti)O-3 Inverse Opals

Synthesis Of (Pb,La)(Zr,Ti)O-3 Inverse Opal Photonic Crystals

Preparation And Characterization Of Plzt Ferroelectric Inverse Opal

Preparation and Characterization of Ferroelectric Inverse Opal Via a Sol-Gel Process

Ferroelectric Inverse Opals with Electrically Tunable Photonic Band Gap

PLZT Inverse Opal Materials Derived from Sol-Gel Process

Preparation and Characterization of Nanocrystalline ZnS/ZnO Doped Silica Inverse Opals

Temperature Tunable Photonic Bandgap in PLZT Inverse Opals

Preparation and Photonic Bandgap Properties of Lead Lanthanum Titanate Inverse Opal Photonic Crystals

Fabrication of Barium Titanate Inverse Opals by Sol-Gel Electrophoretic Deposition Process

Probing photonic effect on photocatalytic degradation of dyes based on 3D inverse opal ZnO photonic crystal

Synthesis and Characterization of Potassium Bismuth Titanate Inverse Opal Photonic Crystals by Sol–gel Technique

Fabrication and property of polystyrene opaline heterostructure

Structure study on barium titanate inverted opals with film morphologies

Solvothermal Synthesis of 3D Photonic Crystals Based on ZnS/opal System

Optimal process of preparation of inverse opal zirconia

Strong Suppression and Enhancement of Photoluminescence in Zn2sio4 : Mn2+ Inverse Opal Photonic Crystals

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Fabricate Photonic Crystals Based on ZnS/opal System Via Solvothermal Method

Preparation and photonic bandgap properties of Na1/2Bi1/2TiO3 inverse opal photonic crystals