Abstract:Clean Si(111)-(7{x7) surfaces, followed by air-exposure, have been investigated by reflection high energy electron diffraction (RHEED) and scanning tunneling microscopy (STM). Fourier transforms (FTs) of STM images show the presence of short range (7x7) order on the air-oxidized surface. Comparison with FTs of STM images from a clean Si(111)-(7x7) surface shows that only the 1/7th order spots are present on the air-oxidized surface. The oxide layer is ~ 2-3 nm thick, as revealed by cross-sectional transmission electron microscopy (XTEM). Growth of Ag islands on these air-oxidized Si(111)-(7x7) surfaces has been investigated by in-situ RHEED and STM and ex-situ XTEM and scanning electron microscopy. Ag deposition at room temperature leads to the growth of randomly oriented Ag islands while preferred orientation evolves when Ag is deposited at higher substrate temperatures. For deposition at 550{\deg}C face centered cubic Ag nanoislands grow with a predominant epitaxial orientation [1 -1 0]Ag || [1 -1 0]Si, (111)Ag || (111)Si along with its twin [-1 1 0]Ag || [1 -1 0]Si, (111)Ag || (111)Si, as observed for epitaxial growth of Ag on Si(111) surfaces. The twins are thus rotated by a 180{\deg} rotation of the Ag unit cell about the Si [111] axis. It is intriguing that Ag nanoislands follow an epitaxial relationship with the Si(111) substrate in spite of the presence of a 2-3 nm thick oxide layer between Ag and Si. Apparently the short range order on the oxide surface influences the crystallographic orientation of the Ag nanoislands.

Reconstruction of Ag Adsorbed on Stepped Si(111) 7×7 Surface

Initial Stages of Ag Adsorption on Si(111)-7 X 7 Surface

Stm Study Of Au Adsorption On Si(111)-7x7 Surface: Voltage And Temperature Dependence

Step Edges As Reservoirs of Ag Adatom Gas on A Si(111) Surface

Pits and Adatoms at the Interface of 1-Ml C-84/Ag (111)

Electronic-Structures Of Ag-Adsorbed Si(111) Surface

Oxygen Adsorption on Ag∕Si(111)-7×7 Surfaces

Identifying the Numbers of Ag Atoms in Their Nanostructures Grown on a Si(111)-(7 × 7) Surface

Two-Dimensional Surface Adatom of Gas Phase and Core-Level Photoemission Spectroscopy

Formation of ordered arrays of Ag nanowires and nanodots on Si(5 5 7) surface

The Study of Ag Adsorbed on Ge(111) 2×1 Surfaces Using First-Principles Calculations

Growth of nanosize Ag dots with uniform height on a Si(111)-7×7-C 2 H 5 OH surface, and their electronic properties

Scanning tunnelling microscope tip-induced reconstruction on Si(111) √3 × √3 R30°-Ag surface

Growth of nanosize Ag dots with uniform height on a Si(111)-7×7-C<sub>2</sub>H<sub>5</sub>OH surface, and their electronic properties

Scanning tunnelling microscopy observations at initial stage of Cs adsorption on Si(111)-[text removed] × [text removed]-Ag surface

Analysis of the Adsorbates and Determination of the Adsorption Sites on Si(1 1 1)-7×7 after a Large Amount of Ar Exposure at Room Temperature

Aggregation of Organic Molecules on Silver Surface with the Balance Between Molecule–substrate Interaction and Intermolecular Interaction

Exploring the Adsorption Mechanism of Tetracene on Ag(110) by STM and Dispersion-Corrected DFT

Scanning Tunnelling Microscopy Observations at Initial Stage of Cs Adsorption on Si(111)‐$\sqrt{3}$ × $\sqrt{3}$‐ag Surface

Growth of epitaxially oriented Ag nanoislands on air-oxidized Si(111)-(7x7) surfaces: Influence of short range order on the substrate

Scanning Tunnelling Microscope Tip-Induced Reconstruction on Si(111) (3) 1/2 ×(3) 1/2 R30°-Ag Surface