Microstructure and Tensile Properties of Isothermally Forged Ni–43Ti–4Al–2Nb–2Hf Alloy

Xiao-Yun Song,Yan Li,Fei Zhang

DOI: https://doi.org/10.1007/s12598-013-0151-9

2013-01-01

Abstract:NiTi–Al-based alloys are promising high-temperature structural materials for aerospace and astronautics applications. A new NiTi–Al-based alloy Ni–43Ti–4Al–2Nb–2Hf (at%) was processed via isothermal forging. The microstructure and mechanical properties at room temperature and high temperature were investigated through scanning electron microscope (SEM), X-ray diffraction (XRD), and tensile tests. Results show that the microstructure of as-forged Ni–43Ti–4Al–2Nb–2Hf alloy consists of NiTi matrix, Ti 2 Ni phase, and Hf-rich phase. The simultaneous addition of Nb and Hf, which have strong affinities for Ti sites, promotes the precipitation of Hf-rich phases along the grain boundaries. The tensile strengths of Ni–43Ti–4Al–2Nb–2Hf alloy are dramatically increased compared with the ternary Ni–46Ti – 4Al alloy. At room temperature and 650 °C, the yield stress of Ni–43Ti–4Al–2Nb–2Hf alloy reaches 1,070 and 610 MPa, respectively, which are 30 % and 150 % higher than those of Ni–46Ti–4Al alloy. The improved tensile property results from the solid solution strengthening by Nb and Hf, as well as the dispersion hardening of the Ti 2 Ni and Hf-rich phases.