Abstract:Electrical explosion, characterized by ultrafast heating (dT/dt ∼ 1011 K/s) and quenching (1010 K/s) rates of the sample, is a powerful tool for synthesizing graphene-related materials. Experiments were performed with graphite plate in water and Cu wire in graphite-powder-contained tube, to determine the influence of the confined environment on the morphology of the products. As a comparison, an Al-coated carbon foil was exploded in free air. High-speed photography along with electrophysical and optical diagnostics were applied to characterize the electrical explosion. Accordingly, SEM, EDS, and XPS were used to characterize the explosion products. The results reveal that the confined environment prevents the discharge channel from expanding or limiting at a certain diameter so that the products quench in a confined environment that is different from free air. In water and tube explosions, due to the shockwave and the expansion of the discharge channel, the graphite products are compacted to the baseplate, namely, the interface of the water medium and tube wall, respectively. Stacked graphite sheets are formed as a result. Based on the high-speed photography and SEM results, the synthesized graphite is partly exfoliated in the confined environments; consequently, thin graphite nanosheet (less than 10 nm) is observed in the marginal areas. The mechanism of exfoliation is preliminarily analysed in water and tube explosion. Furthermore, a composite material is obtained in tube explosion, and the structure is stacked graphite sheets with spherical copper nanopowder adhering to it. As a comparison, when exploding in free air, typical spherical nanoparticles are synthesized for both elements; finally, the discrepant formation mechanisms of products in confined or unconfined environments are simply discussed.

Production of Nanosized Graphite Powders from Natural Graphite by Detonation

Preparation of Nano-Graphite Powder by Explosive Detonation Method

Nano-graphite synthesized by explosive detonation

Nano-Graphite Synthesized by Explosive Detonation and Its Application in Preparing Diamond under High-Pressure and High-Temperature

Preparation of Graphene Nanosheets Through Detonation

The Production of Carbon Nano-Onions and Wheat Stalk Nano-Chains over Stainless Steel Supported La0.95mg0.05ni0.8co0.2o3 Catalyst

Experimental Study on the Hydrogen Storage and Release in Nano-Graphite Synthesized by Explosive Detonation

Methane Catalytic Cracking to Make Hydrogen and Graphitic Nano Carbons (nanotubes, Microfibers, Microballs, Onions) with Zero Emission

A Facile and Efficient Method to Prepare Exfoliated and Reduced Graphene Nanosheets by Detonation

Synthesis and Characterization of Carbon Nanostructures by Evaporating Pure Graphite and Carbon Black in Detonation-Gas Arc Discharge

One-step preparation of pure and Cu-decorated graphite thin layers via electrical explosion in a confined environment: Physical process and product characterization

Measurement and Characterization of Nano-graphite Particles Size

Preparation of Hollow Carbon Nanospheres Via Explosive Detonation

Synthesis of Graphite-coated Copper Nanoparticles by the Detonation of a Copper-doped Emulsion Explosive

Scalable Production of Carbon Encapsulated Ni Nanoparticles by Water Arc Discharge: Structural and Magnetic Properties

Core–Shell Composites Based on Partially Oxidized Blend of Detonation Synthesis Nanodiamonds

Characterization Of The Grain Size Of Nanographite

Synthesis of graphene nanosheets by the electrical explosion of graphite powder confined in a tube

Ultra-fast Self-Assembly and Stabilization of Reactive Nanoparticles in Reduced Graphene Oxide Films

Synthesis of diamond using nano-graphite and Fe powder under high pressure and high temperature

Formation Mechanism for Oxidation Synthesis of Carbon Nanomaterials and Detonation Process for Core-Shell Structure