Analysis on Abnormal Fracture of DWTT Specimen for Pipeline Steel with High Property

YANG Zheng,FENG Yao-rong,CHEN Hong-da,LI Ji-ke

DOI: https://doi.org/10.3969/j.issn.1001-3938.2006.04.005

2006-01-01

Abstract:According to different reason caused the brittle area in fracture on DWTT specimen,the appearance of abnormal fracture can be classified into three kinds,the first is isolated brittle fracture area occurred only in the area within hammering,through longer toughness stable enlarging after toughness starting fracture of sample.The second kind of specimen is to transfer to brittle fracture until sample destroyed and the brittle areas become bigger through toughness stable enlarging after toughness starting fracture of sample,the third kind of specimen shows toughness fracture appearance in initial fracture area and the area within hammering,and brittle fracture area only shown in the middle of specimen.The first and second kind of fracture can be reduced and removed,which caused by compression and distortion in test process and thickness of specimen become larger locally though reducing the maximum load and transverse restriction subject to in fracture process with regards to the third fracture,its transition from toughness to brittle depend on mechanical property of material itself,its occurrence accompanies with actual fracture of pipeline and can not be avoided in test.So,it will cause seriously safety problem to consider all specimens with Abnormal fracture as invalid specimen.