Abstract:MgB2 superconductors with unique microstructures were rapidly fabricated at low temperatures, and exhibited significantly improved critical current density (J(c)). According to the microstructure observations, the prepared samples consisted of lamellar nano MgB2 grains with many embedded nanoimpurities (about 10 nm). The formation of these lamellar nano MgB2 grains is associated with the presence of a local Mg-Cu liquid at sintering temperatures as low as 575 degrees C. The ball milling treatment of the original powders also plays a positive role in the growth of lamellar grains. Based on an analysis of the relationship between resistivity and temperature, the lamellar nano MgB2 grains in the prepared sample possess better grain connectivity than the typical morphology of MgB2 samples prepared by traditional high-temperature sintering. Furthermore, the presence of many nano MgB2 grain boundaries and nano impurities in the prepared sample can obviously increase the flux pinning centers in accordance with the analysis of flux pinning behavior. Both factors mentioned above contribute to the significant improvement in J(c) from low field to relative high field. The method developed in the present work is an effective and low-cost way to further enhance J(c) in MgB2 superconductors across a wide range of applied magnetic fields without using expensive nanometer-sized dopants.

The Improved Superconductive Properties of Mgb2 Bulks with Minor Cu Addition Through Reducing the Mgo Impurity

Significant Improvement in the Critical Current Density of Mgb2 Bulks in Situ Sintered at Low Temperature by Excess Mg Addition

Superconducting Properties of Y2o3/Sic Co-Doped Bulk Mgb2

The Synthesis of Lamellar Nano MgB2 Grains with Nanoimpurities, Flux Pinning Centers and Their Significantly Improved Critical Current Density

MgB2 Superconductor Prepared by Mg Diffusion Method with the Addition of Reduced Graphene Oxide

The Effect of Cu Addition on the Phase Formation and Critical Current Density in the Sugar Doped MgB2 Superconductor

Phase Formation and Superconductive Properties of Cu Doped MgB2 Sintered with Milled B Powder

Improvement of Critical Current Density in MgB2 Superconductors by Zr Doping at Ambient Pressure

Significant Improvement of Jc in MgB2 Bulk Superconductor Using Ball-Milled High-Purity Crystalline Boron

Superconducting properties and growth mechanism of layered structure in MgB 2 bulks with Cu/Y 2 O 3 co-doping

Enhancement of Critical Current Density by a “Mgb2-Mgb4” Reversible Reaction in Self-Sintered Ex-Situ MgB2 Bulks

Excellent Jc in the low-temperature sintered MgB2 superconductors consisted of uncompleted MgB2 phase and residual Mg

The effect of ball-milling treatment of original powders on the sintering process and critical current density of graphite-doped MgB 2 bulks

Effect of addition of nanoparticle TiO2/SiO2 on the superconducting properties of MgB2

Variation of Pinning Mechanism and Enhancement of Critical Current Density in Mgb2 Bulk Containing Self-Generated Coherent Mgb4 Impurity

Enhancement Of The Upper Critical Field In Sub-Micron Carbon-Doped Mgb2 By Two-Step Reaction Method

Superconducting Properties of Ti3SiC2-Doped Bulk MgB2 Superconductor

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor

High Critical Current Density of a MgB 2 Bulk Superconductor High-pressure Synthesized Directly from the Elements

Effects of TiC Doping on the Upper Critical Field of MgB2 Superconductors

Chemical Doping Effect on the Crystal Structure and Superconductivity of Mgb2