Abstract:Hollow spheres assembled by alpha-Co(OH)(2) nanosheets were firstly synthesized through a templated self-assembly solvothermal method, where rationally involved polyvinylpyrrolidone (PVP) is acting as molecular template for nanocrystal geometrical manipulation and ethylene glycol (EG) is acting as both solvent and precipitant for metal cation coordination; followed by subsequent calcinations, mesoporous CO3O4 nanostructures were then topotactic transformed from the primary alpha-Co(OH)(2) by preserving their original frameworks. Such monodisperse hierarchical structure, distributed in diameter of around 2.76 -4.22 mu m, is constructed orderly with several well-aligned nanosheet subunits in a high degree of orientation and separation; moreover, the shell thickness and the void space can be adjusted by changing the concentration of the PVP surfactant. When applying as electrocatalyst for oxygen evolution reaction (OER), the obtained CO3O4 delivered a low onset potential (e.g., around 1.438-1.481 V vs RHE) with a low overpotential (e.g., around 290-310 mV at 10 mAcm(-2)) and relatively small Tafel slopes (e.g., around 86 -97 mV dec(-1)) as well as long-term durability (e.g., up to 99.15% after 10 h) in an alkaline electrolyte. These fine catalytic activities can be attributed to the hierarchical structure with high specific surface area, ordered multilevel pores and void space, which facilitate the electrolyte accessibility and provide more active sites for redox reaction. Therefore, with the presented method, it would be promising for the synthesis of other transition metal oxides/hydroxides with such unique structure towards energy conversion and storage applications. (C) 2018 Published by Elsevier B.V.

Confined Growth of CuO, NiO, and Co3O4 Nanocrystals in Mesoporous Silica (MS) Spheres

Bubble-supported Engineering of Hierarchical CuCo2S4 Hollow Spheres for Enhanced Electrochemical Performance

Single-Crystalline Dendritic Bimetallic And Multimetallic Nanocubes

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

<i>In situ</i> Confinement Growth Strategy for Ordered Mesoporous Carbon Support Ultrasmall MoO<sub>3</sub> Nanoparticles

Synthesis of Morphology-Controllable Mesoporous Co3O4 and CeO2

Micro-morphology highly uniform mesoporous Co3O4 spheres: shape-controlled fabrication by a salt-assisted template-free method and enhanced catalytic performance of styrene epoxidation

Use of Carbonaceous Polysaccharide Microspheres As Templates for Fabricating Metal Oxide Hollow Spheres

Controllable Preparation of Monodisperse Mesoporous Silica from Microspheres to Microcapsules and Catalytic Loading of Au Nanoparticles

Multifunctional Mesoporous Composite Microspheres with Well-Designed Nanostructure: a Highly Integrated Catalyst System.

One-Step Synthesis of Highly Ordered Mesoporous Silica Monoliths with Metal Oxide Nanocrystals in Their Channels

Close-Packed Colloidal SiO2 As a Nanoreactor: Generalized Synthesis of Metal Oxide Mesoporous Single Crystals and Mesocrystals

The Synthesis of a Core–shell Hybrid Composite Micro-Sphere with Controllable Homogenous or Heterogeneous Multi-Shell Structure by Multiple-Growth Via a Combination Method

Preparation of Mesoporous ZnO Microspheres Through a Membrane-Dispersion Microstructured Reactor and a Hydrothermal Treatment

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Confined Growth of CdSe Quantum Dots in Colloidal Mesoporous Silica for Multifunctional Nanostructures

Nanoengineering of Core-Shell Magnetic Mesoporous Microspheres with Tunable Surface Roughness.

Mesoporous microcapsules with noble metal or noble metal oxide shells and their application in electrocatalysis

Controlled Synthesis of N-Doped Carbon Nanospheres with Tailored Mesopores through Self-Assembly of Colloidal Silica.

Synthesis of Mesoporous Co3O4 Nanosheet-Assembled Hollow Spheres Towards Efficient Electrocatalytic Oxygen Evolution

Developing a general method for encapsulation of metal oxide nanoparticles in mesoporous silica shell by unraveling its formation mechanism