Abstract:Pt hollow nanospheres with a particle diameter of 110 nm and a shell thickness of about 5 nm were synthesized in bulk using selenium colloids with a particle diameter of 100 nm as a template. Transmission electron microscopy (TEM), high resolution transmission electron microscopy (HR-TEM), selected area electron diffraction (SAED), X-ray diffraction (XRD), energy dispersive X-ray spectrocopy (EDX), and scanning electron microscopy (SEM) were used to determine their morphologies and structures. The electrocatalytic activity of the Pt hollow nanospheres modifying glassy carbon electrode toward methanol oxidation was measured by using methanol as the probe molecule. We show that the multiporous Pt hollow nanospheres composited of atomic clusters have a uniform particle size, good dispersity, a stable structure, a big surface area and good mass transfer performance. Cyclic voltammetry (CV) showed that when the current density of methanol oxidation was 0.10 mA.cm(-2) and upon positive scanning the methanol oxidation potential of the Pt hollow nanospheres was around 110 and 64 mV negative than that of the Pt solid nanoparticles and Pt black, respectively. Upon negative scanning the former species was about 51 and 13 mV negative than that of the latter two species, respectively. After 800 segments cyclic voltammetry scanning, upon positive scanning the peak current density of methanol oxidation on the Pt hollow nanospheres was found to be 13 and 15 times as high as that of the Pt solid nanoparticles and Pt black, respectively. Upon negative scanning the former species was about 19 and 38 times as high as that of the two latter species. Our experimental results show that the Pt hollow nanospheres have good electrocatalytic activity and stability toward methanol oxidation.

Mesoporous microcapsules with noble metal or noble metal oxide shells and their application in electrocatalysis

Hollow PtPd Nanorods with Mesoporous Shells As an Efficient Electrocatalyst for the Methanol-Oxidation Reaction.

Trimetallic PtPdCo Mesoporous Nanopolyhedra with Hollow Cavities

Pt–Ni–P Nanocages with Surface Porosity As Efficient Bifunctional Electrocatalysts for Oxygen Reduction and Methanol Oxidation

Synthesis of Hollow Platinum-Palladium Nanospheres with a Dendritic Shell As Efficient Electrocatalysts for Methanol Oxidation.

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Localization Of Platinum Nanoparticles On Inner Walls Of Mesoporous Hollow Carbon Spheres For Improvement Of Electrochemical Stability

Tunable Synthesis of Hollow Metal-Nitrogen-Carbon Capsules for Efficient Oxygen Reduction Catalysis in Proton Exchange Membrane Fuel Cells.

Enhanced Oxygen Reduction and Methanol Oxidation Electrocatalysis over Bifunctional PtPdIr Mesoporous Hollow Nanospheres

Novel Hollow Sub-Microspheres with Movable Au Nanoparticles and Excessive Pt Nanoparticles in Core and Silica As Shell

PtPdRh Mesoporous Nanospheres: an Efficient Catalyst for Methanol Electro-Oxidation

Novel, Efficient Hollow Zeolitically Microcapsulized Noble Metal Catalysts

Pt@Mesoporous PtRu Yolk–Shell Nanostructured Electrocatalyst for Methanol Oxidation Reaction

Metallic Mesoporous Nanocomposites For Electrocatalysis

Double shelled hollow nanospheres with dual noble metal nanoparticle encapsulation for enhanced catalytic application.

Surface‐Protected Etching of Mesoporous Oxide Shells for the Stabilization of Metal Nanocatalysts

Preparation Of Hollow Submicrospheres With Ordered Porous Sio2 Shell And Multiple Aupt Nanoalloy Cores And Their High Catalytic Activity

Tri-metallic PtPdAu Mesoporous Nanoelectrocatalysts

Hollow Microporous Organic Capsules Loaded with Highly Dispersed Pt Nanoparticles for Catalytic Applications

Preparation of High Catalytic Platinum Hollow Nanospheres and Their Electrocatalytic Performance for Methanol Oxidation

Direct Synthesis of Bimetallic PtCo Mesoporous Nanospheres As Efficient Bifunctional Electrocatalysts for Both Oxygen Reduction Reaction and Methanol Oxidation Reaction.