Abstract:Abstract Mesoporous Y zeolites were prepared by the sequential chemical dealumination (using chelating agents such as ethylenediaminetetraacetic acid, H 4 EDTA, and citric acid aqueous solutions) and alkaline desilication (using sodium hydroxide, NaOH, aqueous solutions) treatments. Specifically, the ultrasound-assisted alkaline treatment (i.e., ultrasonic treatment) was proposed as the alternative to conventional alkaline treatments which are performed under hydrothermal conditions. In comparison with the hydrothermal alkaline treatment, the ultrasonic treatment showed the comparatively enhanced efficiency (with the reduced treatment time, i.e., 5 min vs. 30 min, all with 0.2 mol·L −1 NaOH at 65°C) in treating the deal-uminated Y zeolites for creating mesoporosity. For example, after the treatment of a dealuminated zeolite Y (using 0.1 mol·L −1 H4EDTA at 100°C for 6 h), the ultrasonic treatment produced the mesoporous zeolite Y with the specific external surface area ( S external ) of 160 m 2 ·g· −1 and mesopore volume ( V meso ) of 0.22 cm 3 ·g −1 , being slightly higher than that by the conventional method (i.e., S extemal = 128 m 2 ·g −1 and V meso = 0.19 cm 3 ·g −1 ). The acidic property and catalytic activity (in catalytic cracking of n -octane) of mesoporous Y zeolites obtained by the two methods were comparable. The ultrasonic desilication treatment was found to be generic, also being effective to treat the dealuminated Y zeolites by citric acid. Additionally, the first step of chemical dealumination treatment was crucial to enable the effective creation of mesopores in the parent Y zeolite (with a silicon-to-aluminium ratio, Si/Al = 2.6) regardless of the subsequent alkaline desilication treatment (i.e., ultrasonic or hydrothermal). Therefore, appropriate selection of the condition of the chemical dealumination treatment based on the property of parent zeolites, such as Si/Al ratio and crystallinity, is important for making mesoporous zeolites effectively.

Deep Dealumination of Ultrafine Nay Zeolite

Dealumination of Y zeolite through an economic and eco‐friendly defect‐engineering strategy

Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

A high‐resolution solid‐state NMR study on nano‐structured HZSM‐5 zeolite

On the Acid-Dealumination of USY Zeolite: a Solid State NMR Investigation

Mechanism Of Dealumination Of Nay Zeolite With Oxalic Acid

Study of dealumination of NaY zeolite with different acids

Using ultrasound to improve the sequential post-synthesis modification method for making mesoporous Y zeolites

Dealumination of RHO zeolite by acid treatment and recrystallization with organic pore filler

On understanding the sequential post-synthetic microwave-assisted dealumination and alkaline treatment of Y zeolite

Study on the Formation of Mesopore During Hydrothermal Dealumination of Y Zeolite

MAS NMR Studies on the Dealumination of Zeolite MCM-22

Synthesis of Ultra-Fine NaA Zeolite by Low-Temperature Hydrothermal Treatment

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Extremely Stable Zeolites Developed via Designed Liquid-Mediated Treatment

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

A defect-based strategy for the preparation of mesoporous zeolite Y for high-performance catalytic cracking

Hierarchical submicrosized Y zeolites prepared by sequential desilication-dealumination post-synthesis modification and their catalytic performance in vacuum gas oil hydrocracking.

Sequential Microwave-Assisted Dealumination and Hydrothermal Alkaline Treatments of Y Zeolite for Preparing Hierarchical Mesoporous Zeolite Catalysts

Effect of dealumination defects on the properties of zeolite Y