Coatings containing hydroxyapatite fabricated by microurc oxidation on pure titanium

于维先,于德珍,马洁,毕文翔
DOI: https://doi.org/10.3969/j.issn.1003-1634.2009.07.002
2009-01-01
Abstract:Objective:To fabricate coatings containing hydroxyapatite with microarc oxidation (MAO)on pure tita- nium. Method:Microarc oxidation was performed by using the pulse power. The electrolyte containing 0.4 M CA and 0.2 M NaH2PO4·2H2O was used in the experiment to fabricate oxide coatings. Anodic current density was 20 A/dm2,and the pulse frequency was 60 Hz for 5 min,10 min,20 min,30 min,60 min,respectively. The phase,morphology and composition of the oxide coatings were monitored with X-ray diffraction (XRD)and scanning electron microscopy (SEM)with energy dispersive X-ray spectrometer (EDS). Result:The chemical compositions of the MAO coatings were Ti,O,Ca and P. The phases of the coatings were composed of rutile TiO2,anatase TiO2,and hydroxyapatite. The thickness of the films increased with the increasing of reacting times. With the increasing of reacting times,the number of micro-pore on the surface of MAO coatings decreased,but pore size and the roughness of surface increased. With the increasing of reacting times,element of Ti decreased,elements of Ca and P increased,element of O unchanged. Hydroxyapatite increased,however,Ti,rutile TiO2 and anatase TiO2 decreased with the increasing of reacting times. Conclusion:The coatings containing rutile TiO2,anatase TiO2,and hydroxyapatite on pure titanium are formed by microarc oxidation. The electrolyte contains 0.4 M CA and 0.2 M NaH2PO·42H2O.
What problem does this paper attempt to address?