Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Neutral templating route to mesoporous structured TiO2

Synthesis and Characterization of Mesoporous TiO2 with Wormhole-Like Framework Structure

Synthesis and characterization of amorphous TiO2 with wormhole-like framework mesostructure

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Preparation Nano TiO2 Mesoporous Material by Soft Template

Template-free Hydrothermal Preparation of Mesoporous TiO2 Microspheres on a Large Scale

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

Synthesis of bi-porous TiO2 with crystalline framework using a double surfactant system

Mesoporous titanium dioxide (TiO2) with hierarchically 3D dendrimeric architectures: formation mechanism and highly enhanced photocatalytic activity.

Characterization of Mesoporous Nanocrystalline TiO2 Photocatalysts Synthesized Via a Sol-Solvothermal Process at a Low Temperature

Synthesis and characterization of ordered hexagonal and cubic mesoporous tin oxides via mixed-surfactant templates route.

Preparation Crystalline Mesoporous Titania at Mild Conditions with Inorganic Titanium Precursors

Ligand‐Assisted Assembly Approach to Synthesize Large‐Pore Ordered Mesoporous Titania with Thermally Stable and Crystalline Framework

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Controlled synthesis of ordered mesoporous C-TiO2 nanocomposites with crystalline titania frameworks from organic-inorganic-amphiphilic coassembly

Synthesis of Ordered Mesoporous TiO<sub>2</sub> on a Composite Surfactant Template