Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Synthesis of size-tunable mesoporous anatase titania spheres by a template-free method

Template-free Hydrothermal Preparation of Mesoporous TiO2 Microspheres on a Large Scale

Simple preparation of sub-micron mesoporous TiO2 spheres consisting of anatase nanocrystals

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Synthesis and Characterization of Mesoporous SrTiO3 Spheres Via a Poly Vinyl Alcohol‐Assisted Hydrothermal Route

Rapid Preparation of Uniform High-Crystallized Mesoporous Titania Spheres without High-Temperature Treatment

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Alkaline hydrothermal synthesis of homogeneous titania microspheres with urchin-like nanoarchitectures for dye effluent treatments.

One-pot Template-Free Synthesis of Mesoporous Boehmite Core–shell and Hollow Spheres by a Simple Solvothermal Route

Scalable Synthesis of Mesoporous Titania Microspheres Via Spray-Drying Method.

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Simultaneous formation of silica-protected and N-doped TiO2 hollow spheres using organic–inorganic silica as self-removed templates

Single‐Crystal‐like Mesoporous SrTiO3 Spheres with Enhanced Photocatalytic Performance

Hydrothermal growth of multi-facet anatase spheres

Mesoporous TiO2 Single Crystals: Facile Shape-, Size-, and Phase-Controlled Growth and Efficient Photocatalytic Performance.

Mesoporous hollow sphere titanium dioxide photocatalysts through hydrothermal silica etching

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

Preparation of Large-Pore Mesoporous Nanocrystalline TiO2 Thin Films with Tailored Pore Diameters

Synthesis of easily shaped ordered mesoporous titanium-containing silica

Mesoporous TiO2 Microspheres with Precisely Controlled Crystallites and Architectures