Ferromagnetic Resonance Frequency Tuning of Fetan Thin Films by Strips Patterning with Angular Displacements

C. Y. Tan,X. Chen,Y. G. Ma,Y. Liu,Z. W. Liu,C. K. Ong

DOI: https://doi.org/10.1088/0022-3727/40/22/005

2007-01-01

Abstract:FeTaN thin films with uniaxial anisotropy were fabricated by sputtering and patterned into strips with width of 21 mu m, separation gap of 10 mu m and angular displacement of 0 degrees to 90 degrees from the magnetic easy axis of the unpatterned films. The effective magnetic anisotropy field was effectively modified in both value and direction dependent on the displacement angle. The unpatterned thin films had a maximum permeability of mu 'similar to 700, mu ''similar to 1000 and a ferromagnetic resonance frequency of similar to 1.1 GHz. After patterning, the ferromagnetic resonance frequency was found to be ranging from 1 to 1.8 GHz as the angular displacement was varied, indicating that this method is a viable way of tuning the ferromagnetic resonance frequency. These results were well explained according to the well-known Kittel's formula assuming two fold anisotropies in the patterned films.