Epitaxial Growth of Multilayered YBa/sub 2/cu/sub 3/o//sub 7-Γ//y/sub 0.7/ca/sub 0.3/ba/sub 2/cu/sub 3/o//sub 7-Γ/ Films for High Current Application

Y Lin,Z Wu,X Chen,DX Huang,XH Chen,R Hor,SW Liu,A Jacobson,CL Chen
DOI: https://doi.org/10.1109/tasc.2003.812020
IF: 1.9489
2003-01-01
IEEE Transactions on Applied Superconductivity
Abstract:Multilayered YBa2Cu3O7-delta (YBCO)/Y0.7Ca0.3Ba2Cu3O7-delta (YCBCO) films were epitaxially grown on (001) LaAlO3 and (001) SrTiO3 by using pulsed laser ablation. Constant-high critical current density (J(c)) of 106 A/cm(2) at 77 K has been achieved with the combination of multilayered YBCO and YCBCO layers for films with various thickness. The critical current density exhibits a high constant value for the multilayered structures indicating that the J(c) in the superconductor films no longer decreases with the increase of the film thickness. The result verifies the model that interfaces can limit the density of dislocations that form in the film during the film growth. The artificial multilayered structures terminate the dislocations and the superconductive films at the optimal J(c) conditions maintain a constant high J(c) at various film thickness.
What problem does this paper attempt to address?