Abstract:Surface texturing-plasma nitriding duplex treatment was conducted on AISI 316 stainless steel to improve its tribological performance. Tribological behaviors of ground 316 substrates, plasma-nitrided 316 (PN-316), surface-textured 316 (ST-316), and duplex-treated 316 (DT-316) in air and under grease lubrication were investigated using a pin-on-disc rotary tribometer against counterparts of high carbon chromium bearing steel GCr15 and silicon nitride Si₃N₄ balls. The variations in friction coefficient, mass loss, and worn trace morphology of the tested samples were systemically investigated and analyzed. The results showed that a textured surface was formed on 316 after electrochemical processing in a 15 wt % NaCl solution. Grooves and dimples were found on the textured surface. As plasma nitriding was conducted on a 316 substrate and ST-316, continuous and uniform nitriding layers were successfully fabricated on the surfaces of the 316 substrate and ST-316. Both of the obtained nitriding layers presented thickness values of more than 30 μm. The nitriding layers were composed of iron nitrides and chromium nitride. The 316 substrate and ST-316 received improved surface hardness after plasma nitriding. When the tribological tests were carried out under dry sliding and grease lubrication conditions, the tested samples showed different tribological behaviors. As expected, the DT-316 samples revealed the most promising tribological properties, reflected by the lowest mass loss and worn morphologies. The DT-316 received the slightest damage, and its excellent tribological performance was attributed to the following aspects: firstly, the nitriding layer had high surface hardness; secondly, the surface texture was able to capture wear debris, store up grease, and then provide continuous lubrication.

Research on Surface Treatment Process of Aerospace Flywheel Bearing by Nitrogen Ion Implantation

Surface Modification of Aerospace Flywheel-Bearings by Nitrogen Plasma Immersion Ion Implantation

Research on Improvement of Surface Treatment Process of Aerospace Flywheel Bearing by Diamond-like Carbon

A Study of the Corrosion Resistance of M50NiL Bearing Steel by Ion Implantation

Effect of Dose Rate on Tribological Properties of 8Cr4Mo4V Subjected to Plasma Immersion Ion Implantation

Improvement of nitrogen ion implantation on the wear and corrosion resistance of bearing steel in NaCl solution

Improvement of Impact Wear Performance of Ti6Al4V Alloy by Nitrogen Ion Implantation and Nitriding

Effect Of Hybrid Surface Treatment Composed Of Plasma Nitriding And W-Cr-Ti-Al-N Coating On Tribological Behavior Of Aisi 316l Steel

Surface Texturing-Plasma Nitriding Duplex Treatment for Improving Tribological Performance of AISI 316 Stainless Steel

MODIFICATION OF TRIBOLOGICAL CHARACTERISTICS OF METALS AFTER NITROGEN IMPLANTATION

Nitrogen Ion Implantation on the Mechanical Properties of Aisi 420 Martensitic Stainless Steel

Improvement in the graphite electrode wear characteristic of electrical discharge machined Nimonic 90 through plasma nitriding, laser hardening and duplex process

Effect of Post-Plasma Nitrocarburized Treatment on Mechanical Properties of Carburized and Quenched 18Cr2Ni4WA Steel

In Vitro Corrosion Behavior of TiN Layer Produced on Orthopedic Nickel–titanium Shape Memory Alloy by Nitrogen Plasma Immersion Ion Implantation Using Different Frequencies

Growth of CrN Films by Plasma Ion Implantation & Deposition Based on High Power Pulsed Magnetron Discharge

Effects of ultrasonic surface rolling processing and plasma nitriding on the fretting wear behavior of Inconel 690TT

Plasma Nitriding of AISI 304 Stainless Steel in Cathodic and Floating Electric Potential: Influence on Morphology, Chemical Characteristics and Tribological Behavior

Surface Modification of Polymeric Materials by Plasma Immersion Ion Implantation

Tribological Performance of Surface Treated Piston Assembly with Infiltrated Layer

Effect of N+ Implantation on Surface Characteristics of 316L Stainless Steels for Bipolar Plate in PEMFC

Effects of Nitrogen Ion Implantation and Implantation Energy on Surface Properties and Adhesion Strength of TiN Films Deposited on Aluminum by Magnetron Sputtering