Abstract:For the first time, tricobalt tetraoxide (Co3O4) particles with a well-defined octahedral structure and a size more than 8 mu m were prepared via an ionic liquid-present dissolving-drying-calcination method using cobaltous acetate tetrahydrate (Co(CH3COO)(2)center dot 4H(2)O) as the precursor in this work. Different from the previous works, a kind of ionic liquids (ILs) was employed as one main component of the preparation solution. The materials prepared in the presence of 1-butyl-3-methylimidazolium bromide, 1-butyl-3-methylimidazolium tetrafluoroborate and 1-butyl-3-methylimidazolium chloride were respectively nominated as material a, b and c. As indicated by the XRD and XPS analysis, CoO and Co3O4 were the major components of material a and b, and Co3O4 was the main substance of material c. As confirmed by the obtained SEM images, octahedral particles of Co3O4 with a size greater than 8 mu m were prepared in material c. When being used as anode materials for lithium ion batteries (LIBs), material a, b and c at the current density of 100 mA g(-1) exhibited an initial discharge capacity of 600, 612 and 878 mAh respectively. Particularly, material c was able to deliver a discharge capacity of 336 mAh g(-1) after 10 cycles even under the current density of 500 mA g(-1). A fact that octahedral particles of Co3O4 with a size more than 8 mu m could be prepared using an ionic liquid-present method was presented in this work, which was very beneficial to the development of metal oxides based anode materials of LIBs as well as the exploration of micro-devices.

High Performance Lithium Cobalt Oxides Prepared in Molten KCl for Rechargeable Lithium-Ion Batteries

Analysis of High Rate Performance of Nanoparticled Lithium Cobalt Oxides Prepared in Molten KNO3 for Rechargeable Lithium-Ion Batteries

Cathode Materials of Li_xCo_(0.8)Ni_(0.2)O_2 for Lithium-ion Battery

Study on the Preparation and Electrochemical Performance of LiCoO2

Synthesis of LiMn1/3Ni1/3Co1/3O2 in Molten KCl for Rechargeable Lithium-Ion Batteries

High Performances of Ultrafine and Layered LiCoO2 Powders for Lithium Batteries by a Novel Sol–gel Process

An Ionic Liquid-Present Method for Preparing Micro-sized Octahedral Particles of Co3O4 and Their Applications As Anode Materials for Lithium Ion Batteries

Phase-Controlled Synthesis Of Cobalt Sulfides For Lithium Ion Batteries

Electrochemical Evaluation and Modification of Commercial Lithium Cobalt Oxide Powders

From Metal to Cathode Material: in situ Formation of LiCoO2 with Enhanced Cycling Performance and Suppressed Phase Transition

Highly active cathode material LiCoO_2 for lithium ion battery through β-Co(OH)_2 as precursors

Shale-like Co₃O₄ for High Performance Lithium/sodium Ion Batteries

High performance Li 2 MnSiO 4 prepared in molten KCl–NaCl for rechargeable lithium ion batteries

High-performance of LaCoO3/Co3O4 Nanocrystal As Anode for Lithium-Ion Batteries

Synthesis of LiCoO<sub>2</sub> Powder by Auto-Ignited Combustion of Citrate–Metal Nitrate Precursor

Preparation of LiCoO 2 concaved cuboctahedra and their electrochemical behavior in lithium-ion battery

Hollow Co3o4 Thin Films As High Performance Anodes for Lithium-Ion Batteries

Preparation and Characterization of High-Density Spherical Licoo2 Cathode Material for Lithium Ion Batteries

Lithium Cobalt Oxides Functionalized by Conductive Al-doped ZnO Coating As Cathode for High-performance Lithium Ion Batteries

Facile Synthesis and Li-Electroactivity of Cobalt Oxide Based on Resources Recovered from Waste Lithium-Ion Batteries

CoOOH as Cathode Catalyst for High Performance Non-Aqueous Li-O-2 Batteries