Study on the Structure and Property of the Low Carbon Steel Part Based on the Rapid Prototyping Technique of Welding

朱政强,张华,胡瑢华,徐健宁,付明丽

DOI: https://doi.org/10.3969/j.issn.1002-025x.2008.03.005

2008-01-01

Abstract:The structure and the hardness of the low carbon steel part based on the rapid prototyping technique of welding were studied. The deposition experiments were done on the parent metal Q235 with the technique of gas tungsten arc welding, which was named the TIG welding. The suitable welding speed, welding current and feeding current of the welding wire were selected. The structure and the hardness were analyzed. The results of the experiments showed that the microstructure of the weld seam was ferrite and pearlite. The grain in the single layer was coarse. It was seen from the experiments of the double layers and the more layers that the grain in the middle layer was fine. It was more obviously from the deposited part. So it can smooth the crystal and fine the grain in the weld seam microstructure using the technique of multi-layer welding. The parts which were formed perfectly were obtained. Because the back-layer weld seam can heattreat the front-layer weld seam. The hardness of the parent metal was the lowest. The middle weld seam was softened because of the back weld seam temper to the front. The hardness of the surface layer was the highest. It approached to the real hardness.