Abstract:A novel heterogeneous structure welded joint was developed by joining low carbon steel (LCS) with hypereutectic high-chromium white cast iron (HCWCI). The tensile strength and ductility of LCS are 470.3 MPa and 25.3%, while that of HCWCI are 460.5 MPa and 1.6%, respectively. Additionally, tensile test results show that the welded joint exhibited the superb synergy of the tensile strength of 445.6 MPa and the ductility of 12.5%. These achievements can be primarily attributed to the presence of multi-level deformation mechanisms resulting from the heterogeneous structures. The study also investigated the impact of microstructural changes in the diffusion zone after postweld heat treatment (PWHT). The findings reveal that the reduction in hardness and tensile strength is mainly due to the transformation of carbides in the diffusion zone. This research sheds light on the potential of employing heterogeneous structures in welded joint, serving as a valuable guide for optimizing the mechanical performance of a broad spectrum of alloys in lightweight engineering applications.

A novel low carbon steel/hypereutectic high-chromium white cast iron welded joint with heterogeneous structure