Abstract:By using chemical reduction-deposition method,a metallic nickel-decorated multi-walled carbon nanotube material,symbolized as x%Ni/CNTs,was prepared.TEM and XRD measurements demonstrated that the metallic nickel was evenly coated onto the carbon nanotube substrate,with granule-diameter of the Ni_x~0-crystallites at ～12 nm.The H_2-TPD and CO-TPD measurements showed that the modification of metallic nickel to the CNTs resulted not only in a significant increase in the total amounts of its adsorbing hydrogen and CO,but also in pronounced enhance of the proportion of the dissociatively adsorbed hydrogen H(a) and strongly chemisorbed CO(a) in their respective total amount of adsorption.With this composite nano-carbon material as an additive,a co-precipitated Cu_6Zn_3Al_1-12.5%(8%Ni/CNT) catalyst was prepared.The assay of its catalytic activity for methanol synthesis from syngas showed that under the reaction conditions of 2.0 MPa,V(H_2)/V(CO)/V(CO_2)/V(N_2)=62/30/5/3,GHSV=2 700 mL(STP)·h~(-1)·(g-catal.)~(-1),the observed CO conversion and methanol STY reached 34% and 442 mg·h~(-1)·(g-catal.)~(-1),which was about 38% and 17% higher than those over the Cu_6Zn_3Al_1 and Cu_6Zn_3Al_1-12.5%CNT catalysts, respectively,at the respective optimal operation temperature,513 K and 503 K.The results of the present work indicated that the nickel-modified CNTs could serve as a promoter more excellent than the simple CNTs.Its unique feature of promoting adsorption/spillover of hydrogen and CO would be beneficial to generating microenvironments with higher stationary-state concentration of active hydrogen-adspecies and chemisorbed CO(a) on surface of the functioning catalyst,and thus be favorable to increasing the rate of the CO hydrogenation reactions.

One-step Preparation of Carbon Nanotubes with Nickel As the Core

A Facile Synthesis of C-N Hollow Nanotubes As High Electroactivity Catalysts of Oxygen Reduction Reaction Derived from Dicyandiamide

Preparation, Mechanical and Electrical Properties of Carbon Micro- and Nanocoils

Reticular Nickel Microwires with Assembled Nanostructures: Synthesis, Magnetism and Catalysis for the Growth of Carbon Nanotubes

Functionalization of carbon nanotubes with magnetic nanoparticles: general nonaqueous synthesis and magnetic properties.

Fabrication and growth mechanism of Ni-filled carbon nanotubes by the catalytic method

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

In Situ Preparation of Nickel/carbon Core–shell Structure by Chemical Vapor Deposition

Preparation and Characterization of a Material of Carbon Nanotubes Decorated by Nickel

Ni/Ni3C Core-Shell Nanochains and Its Magnetic Properties: One-Step Synthesis at low temperature

Synthesis Of Nickel Nanoparticles And Carbon Encapsulated Nickel Nanoparticles Supported On Carbon Nanotubes

Influence of one-pot and two-step preparation on the quality of carbon nanotubes using pine sawdust as the catalyst support

Preparation and Characteristics of Core–shell Structure Nickel/silica Nanoparticles

Preparation and Magnetic Properties of Cu-Ni Core-Shell Nanowires in Ion-Track Templates

One-Pot Synthesis of One-Dimensional Array Pt Nanoparticles on Carbon Nanotubes Via A Facile Microwave Polyol Method

Controllable preparation of Ni nanoparticles for catalysis of coiled carbon fibers growth.

Carbon Nanotubes Filled with Metallic Nanowires

Facile Preparation and Magnetic Properties of Ni Nanotubes in Polycarbonate Ion-Track Templates

Preparation and Characterization of Ni Nanoparticles Filled Carbon Nanotubes

Facile and rapid synthesis of nickel nanowires and their magnetic properties

Carbon nanotubes filled partially or completely with nickel