Abstract:Novel amphoteric pH-sensitive hydrogels with pendant carboxyl and backbone tertiary amine groups were designed and synthesized. First, ethylenediaminetetraacetic dianhydride (EDTAD) reacted with butanediamine (BDA) via N-acylation reaction to give a polyamide prepolymer with pendant carboxyl groups (PEB–COOH); then amino-terminated poly(ethylene glycol) 500 (ATPEG500) was added as a cross-linking agent to produce the desired network polymer (PEB–ATPEG500–COOH). The obtained hydrogels are potentially degradable and non-toxic since its backbone and cross-linking sections are both linked by amide bonds and all monomers have been proved as safe. FTIR, 1H NMR, 13C NMR and ninhydrin reaction method were employed to qualitatively and quantitatively characterize the obtained polymers. The effect of cross-linking agent amount, characterized by the molar ratios (Rm) of NH2 groups in ATPEG500 to pendant COOH groups in PEB–COOH, on the swelling behavior of the proposed hydrogel was examined. The results indicate that the equilibrium swelling ratio decreases and the pH-sensitivity becomes retarded with the increase of Rm. For PEB–ATPEG500–COOH hydrogels with Rm no more than 0.42, they exhibited three SRe variation zones at pH 2–4, pH 6–7 and pH 9–11, respectively, suggesting obvious and interesting amphoteric pH-sensitivity. In addition, the swelling kinetics tests on PEB–ATPEG500–COOH with Rm=0.32 reveal that the swelling kinetics of proposed hydrogel follows a Fickian diffusion process in media of pH 7, and an anomalous diffusion process in media of pH 2 and 11. The above obtained results will facilitate the application of this proposed hydrogel in biomedical fields, particularly in the drug controlled release.

Synthesis and Characterization of Intelligent PMAA Polymer Hydrogels

Synthesis of Novel pH-Sensitive Poly(methacrylic acid-co-acrylamide)Hydrogels and their Swelling Behavior

Study of the Properties of Hydrolyzed Polyacrylamide Hydrogels with Various Pore Structures and Rapid Ph-Sensitivities

Synthesis and characterization of pH and temperature sensitive hydrogel based on poly(N-isopropylacrylamide), poly(ɛ-caprolactone), methylacrylic acid, and methoxyl poly(ethylene glycol)

Fabrication of Novel Temperature and Ph Sensitive Poly (N-Isopropylmaleamic Acid-Co-acrylonitrile) Hydrogels

Ultrasonic Synthesis of Ph-Sensitive Pmaa Hydrogel

Poly(Maleic Anhydride-Co-Acrylic Acid)/Poly(Ethylene Glycol) Hydrogels with Ph- and Ionic-Strength-Responses

Synthesis and properties of pH and temperature sensitive P(NIPAAm-co-DMAEMA) hydrogels.

Temperature and Ph Response, and Swelling Behavior of Porous Acrylonitrile-Acrylic Acid Copolymer Hydrogels

Synthesis and Property of Temperature and Ph Sensitive Xanthan-Ma/pnipaam Hydrogels

Preparation, properties, and drug release of thermo- and pH-sensitive poly((2-dimethylamino)ethyl methacrylate)/poly( N , N -diethylacrylamide) semi-IPN hydrogels

Investigation Of Swelling And Controlled-Release Behaviors Of Hydrophobically Modified Poly(Methacrylic Acid) Hydrogels

Preparation and Swelling Behavior of Ph/temperature Responsive Semi-Ipn Hydrogel Based on Carboxymethyl Xylan and Poly(n-Isopropyl Acrylamide)

Synthesis of Ph-Responsive Hydrophobically-Modified Hydrogels of Poly(methacrylic Acid-Co-diallylammonium Salt) in Aqueous Solution

Synthesis and Swelling Characteristics of Ph and Thermoresponsive Interpenetrating Polymer Network Hydrogel Composed of Poly(Vinyl Alcohol) and Poly(Acrylic Acid)

Novel amphoteric pH-sensitive hydrogels derived from ethylenediaminetetraacetic dianhydride, butanediamine and amino-terminated poly(ethylene glycol): Design, synthesis and swelling behavior

pH-responsive semi-interpenetrating networks hydrogels of poly(acrylic acid-acrylamide-methacrylate) and amylose. I. Synthesis and characterization

Preparation and pH-sensitive swelling behavior of physically crosslinked polyampholyte gels

Study on Novel Hydrogels Based on Thermosensitive PNIPAAm with Ph Sensitive PDMAEMA Grafts.

Preparation of macroporous polyvinyl alcohol formaldehyde based hydrogels and their dual thermo- and pH-responsive behavior

Synthesis and characterization of biodegradable pH-sensitive hydrogels based on poly(ɛ-caprolactone), methacrylic acid, and poly(ethylene glycol)☆