Abstract:A kind of novel hydrogels, poly(methacrylic acid-co-acrylamide) [poly(MAA-co-AM)], were prepared by radical aqueous copolymerization of acrylamide and methacrylic acid in the presence of crosslinker N-N′-methylenebisacrylamide (BIS). The swelling dynamics of the prepared dry hydrogels were investaged. The results show that the swelling behaviors of the prepared hydrogels are different with the different contents of methacrylic acid (MAA) in the hydrogels, and the swelling ratio of the hydrogels prepared increases with the increase of pH value of the solution. When the prepared hydrogels were shifted between solutions with pH=2 and pH=12, the hydrogels exhibit rapid reversible swelling-deswelling property, and their responsive rates are affected significantly by stirring. The hydrogels with absorbed water in equilibrium can be deswelled in both acid and alkaline solutions, they shrink more than 90% in solution of pH=2 within 10 min, and the shrinking rates decrease with the increase of pH value of the solution. The swelling properties of prepared hydrogels in NaCl and CaCl 2 solutions were investigated; the results show that the influences of the ionic strength and the charge of counter ion in the solution are obvious, and that the hydrogels display the reversible swelling-deswelling property in water and NaCl solution.

Ultrasonic Synthesis of Ph-Sensitive Pmaa Hydrogel

Synthesis of Novel pH-Sensitive Poly(methacrylic acid-co-acrylamide)Hydrogels and their Swelling Behavior

Study of the Properties of Hydrolyzed Polyacrylamide Hydrogels with Various Pore Structures and Rapid Ph-Sensitivities

Synthesis of Macroporous Poly(n‐isopropylacrylamide) Hydrogel with Ultrarapid Swelling–deswelling Properties

Synthesis of Ph-Responsive Hydrophobically-Modified Hydrogels of Poly(methacrylic Acid-Co-diallylammonium Salt) in Aqueous Solution

Synthesis and Characterization of Intelligent PMAA Polymer Hydrogels

Temperature and Ph Response, and Swelling Behavior of Porous Acrylonitrile-Acrylic Acid Copolymer Hydrogels

Investigation Of Swelling And Controlled-Release Behaviors Of Hydrophobically Modified Poly(Methacrylic Acid) Hydrogels

Radiation Synthesis and Characterization of Polydmaema Hydrogel

Synthesis and characterization of temperature- and pH-sensitive poly[2-(N,N-dimethylamino)ethyl methacrylate-g-nisopropylacrylamide] hydrogels

Synthesis and Characterization of a Ph‐ and Ionic Strength‐Responsive Hydrogel

Poly(Maleic Anhydride-Co-Acrylic Acid)/Poly(Ethylene Glycol) Hydrogels with Ph- and Ionic-Strength-Responses

Swelling behaviour of a new kind of polyampholyte hydrogel composed of dimethylaminoethyl methacrylate and acrylic acid

Research on Synthesis and Properties of Ph/thermo-Sensitive Hydrogel

Synthesis and characterization of temperature- and pH-sensitive pPoly(N,N-diethylacrylamide-co-methacrylic acid) hydrogels with expanded conformations

Synthesis and properties of pH and temperature sensitive P(NIPAAm-co-DMAEMA) hydrogels.

Study on mechanical performance of PDMAEMA hydrogel with pH and temperature sensitivity

Synthesis and Characterization of Poly(n-Tert-butylacrylamide-co-acrylamide) Hydrogel with Enhanced Responsive Properties

Swelling Properties of Ph-Responsive Hydrophobically Modified Hydrogels of Poly(Methacrylic Acid-Co-Diallylammonium Salt) in Aqueous Solution

Synthesis of pH-sensitive sulfonamide-based hydrogels with controllable crosslinking density by post thermo-curing

Preparation And Ph-Responsive Performance Of Silane-Modified Poly(Methylacrylic Acid)